Properties
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 1.55 g/cm³ Show Supplier Material materials with Density of 1.55 g/cm³ | ISO1183 |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongation | 23.0 °C | 6.5 % Show Supplier Material materials with Elongation of 6.5 % | ISO527 |
Flexural modulus | 23.0 °C | 11 GPa Show Supplier Material materials with Flexural modulus of 11 GPa | ISO178 |
Flexural strength | 23.0 °C | 295 MPa Show Supplier Material materials with Flexural strength of 295 MPa | ISO178 |
Impact strength, Charpy notched | 23.0 °C | 18 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 18 kJ/m² | ISO179 |
Impact strength, Charpy unnotched | 23.0 °C | 100 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 100 kJ/m² | ISO179 |
Tensile strength | 23.0 °C | 210 MPa Show Supplier Material materials with Tensile strength of 210 MPa | ISO527 |
Thermal
| Property | Value | Comment | |
|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 247 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 247 °C | ISO 75/A | |
Melting point | 266 - 270 °C Show Supplier Material materials with Melting point of 266 - 270 °C | ISO3146 | |
Flammability | HB UL94 | ||
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dielectric strength | 23.0 °C | 23 kV/mm Show Supplier Material materials with Dielectric strength of 23 kV/mm | GB/T 1408 |
Volume resistivity | 23.0 °C | 1.00E+17 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+17 Ω·cm | GB/T1410 |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Automotive industry, machinery shields, military products, building materials, etc. | |
| Fillers | 50% Glass Fiber | |