Properties
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 1.39 g/cm³ Show Supplier Material materials with Density of 1.39 g/cm³ | ISO1183 |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongation | 23.0 °C | 6 % Show Supplier Material materials with Elongation of 6 % | ISO527 |
Flexural modulus | 23.0 °C | 8.5 GPa Show Supplier Material materials with Flexural modulus of 8.5 GPa | ISO178 |
Flexural strength | 23.0 °C | 275 MPa Show Supplier Material materials with Flexural strength of 275 MPa | ISO178 |
Hardness, Rockwell L | 23.0 °C | 106 [-] Show Supplier Material materials with Hardness, Rockwell L of 106 [-] | ISO 2039 |
Hardness, Rockwell M | 23.0 °C | 95 [-] Show Supplier Material materials with Hardness, Rockwell M of 95 [-] | ISO 2039 |
Hardness, Rockwell R | 23.0 °C | 115 [-] Show Supplier Material materials with Hardness, Rockwell R of 115 [-] | ISO 2039 |
Impact strength, Charpy notched | 23.0 °C | 12 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 12 kJ/m² | ISO179 |
Impact strength, Charpy unnotched | 23.0 °C | 70 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 70 kJ/m² | ISO179 |
Tensile strength | 23.0 °C | 185 MPa Show Supplier Material materials with Tensile strength of 185 MPa | ISO527 |
Thermal
| Property | Value | Comment |
|---|---|---|
Heat deflection temperature, 1.80 MPa | 254 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 254 °C | ISO 75/A |
Melting point | 265 - 270 °C Show Supplier Material materials with Melting point of 265 - 270 °C | ISO3146 |
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Volume resistivity | 23.0 °C | 1.00E+17 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+17 Ω·cm | GB/T1410 |
Rheological Properties
| Property | Value | Comment |
|---|---|---|
Melt mass-flow rate | 23 g/10min Show Supplier Material materials with Melt mass-flow rate of 23 g/10min | ISO 1133 |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Automotive industry, machinery shields, military products, building materials, etc. | |
| Fillers | 33% Glass Fiber | |