Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.39 g/cm³ Show Supplier Material materials with Density of 1.39 g/cm³ | ISO1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elongation | 23.0 °C | 7 % Show Supplier Material materials with Elongation of 7 % | ISO527 |
Flexural modulus | 23.0 °C | 8 GPa Show Supplier Material materials with Flexural modulus of 8 GPa | ISO178 |
Flexural strength | 23.0 °C | 275 MPa Show Supplier Material materials with Flexural strength of 275 MPa | ISO178 |
Impact strength, Charpy notched | 23.0 °C | 15 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 15 kJ/m² | ISO179 |
Impact strength, Charpy unnotched | 23.0 °C | 95 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 95 kJ/m² | ISO179 |
Tensile strength | 23.0 °C | 185 MPa Show Supplier Material materials with Tensile strength of 185 MPa | ISO527 |
Thermal
Property | Value | Comment |
---|---|---|
Melting point | 263 - 270 °C Show Supplier Material materials with Melting point of 263 - 270 °C | ISO3146 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Volume resistivity | 23.0 °C | 1.00E+17 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+17 Ω·cm | GB/T1410 |
Technological properties
Property | ||
---|---|---|
Application areas | For high-speed railway | |
Fillers | 34% Glass Fiber |