DuraSense Recycled S30 Black

Alternative and trade names
PP-WF30
Want to keep this datasheet? Save it now in your required format

Description

Recycled Polypropylene (PP) reinforced with 30% S-Wood fiber (Biocomposite).

This grade is also available as biobased polypropylene (PP).

Physical properties are measured at 23°C and 50% RH

Related Standards

This material data has been provided by Stora Enso Biocomposites.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Bio-based content

30.0 %

Show Supplier Material materials with Bio-based content of 30.0 %

Density

23 °C

1.02 g/cm³

Show Supplier Material materials with Density of 1.02 g/cm³

ISO 1183

Recycled Content

70.0 %

Show Supplier Material materials with Recycled Content of 70.0 %

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23 °C

3 GPa

Show Supplier Material materials with Elastic modulus of 3 GPa

ISO 527-2/2

Elongation

23 °C

3.1 %

Show Supplier Material materials with Elongation of 3.1 %

ISO 527-2/50

Flexural modulus

23 °C

2.8 GPa

Show Supplier Material materials with Flexural modulus of 2.8 GPa

ISO 527-2/2

Impact strength, Charpy unnotched

23 °C

16 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 16 kJ/m²

ISO 179/1eU

Tensile strength

23 °C

36 MPa

Show Supplier Material materials with Tensile strength of 36 MPa

ISO 527-2/50

Thermal

PropertyValue

Flammability

UL94: HB

Technological properties

Property
Certifications

  • Chemical substances: REACH Compliant
  • Raw material: FSC/PEFC™ Chain of Custody
  • Food Applications: EU10/2011, GB4806.6-2016
  • Production: Approved according to GMP (Good Manufacturing Practice)
  • Toys: EN 71-3, GB 6675.1-2014
  • ISO certifications: ISO 9001/14001/50001/ OHSAS18001
  • International Sustainability and Carbon Certification: ICSS Plus
  • Fillers

    30% S-Wood Fiber

    Other

    General safety instructions, read also Process instructions:

  • Avoid high temperatures an long residence time. At high temperature fibers may degrade and can result in pressure build up in machine.
  • Avoid large piles of purged material, can start to smolder
  • Keep reject material from flammable materials, let cool before disposal i.e in water
  • Processing methods

    Drying: 4 hours at 105°C

    Injection moulding machine Temperatures:

  • Nozzle temp: 180 - 205°C
  • Zones used: 180 - 200°C
  • Zones unused: 150 - 180°C
  • Hot runner: 180 - 205°C
  • Mold temperature: 40-100°C

  • The below instructions may differ on due to injection speed, machine etc. Read process intructions.

  • Injection speed: Medium to fast
  • Holding pressure: At least 50% of injection pressure
  • Holding time: Until gate freeze or lower
  • Cooling time: Approx 2 sek/mm wall thickness
  • Shot size: 25-75% of machine capacity, increase shot by approx. 10% compared to unfilled polymer