Dimension
Property | Value |
---|---|
Length | 3000 - 6000 mm Show Supplier Material materials with Length of 3000 - 6000 mm |
Thickness | 2 - 50 mm Show Supplier Material materials with Thickness of 2 - 50 mm |
Width | 1500 - 2000 mm Show Supplier Material materials with Width of 1500 - 2000 mm |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Charpy impact energy, V-notch | -46.0 °C | 45 J Show Supplier Material materials with Charpy impact energy, V-notch of 45 J | |
Elongation | 23.0 °C | 25 % Show Supplier Material materials with Elongation of 25 % | |
Hardness, Brinell | 23.0 °C | 290 [-] Show Supplier Material materials with Hardness, Brinell of 290 [-] | |
Tensile strength | 23.0 °C | 630 - 690 MPa Show Supplier Material materials with Tensile strength of 630 - 690 MPa | |
Yield strength Rp0.2 | 23.0 °C | 420 - 500 MPa Show Supplier Material materials with Yield strength Rp0.2 of 420 - 500 MPa | T<13MM (Min), T≥13MM (Max) |
Chemical properties
Property | Value |
---|---|
Carbon | 0.03 % Show Supplier Material materials with Carbon of 0.03 % |
Chromium | 22 - 24 % Show Supplier Material materials with Chromium of 22 - 24 % |
Copper | 0.1 - 0.6 % Show Supplier Material materials with Copper of 0.1 - 0.6 % |
Iron | Balance |
Manganese | 2 % Show Supplier Material materials with Manganese of 2 % |
Molybdenum | 0.1 - 0.6 % Show Supplier Material materials with Molybdenum of 0.1 - 0.6 % |
Nickel | 3.5 - 5.5 % Show Supplier Material materials with Nickel of 3.5 - 5.5 % |
Nitrogen | 0.05 - 0.2 % Show Supplier Material materials with Nitrogen of 0.05 - 0.2 % |
Other | B: 35 PPM |
Phosphorus | 0.04 % Show Supplier Material materials with Phosphorus of 0.04 % |
Silicon | 1 % Show Supplier Material materials with Silicon of 1 % |
Sulfur | 0.015 % Show Supplier Material materials with Sulfur of 0.015 % |
Technological properties
Property | ||
---|---|---|
Application areas | The main applications are for details with special requirements for high corrosion resistance. | |
Corrosion properties | Good resistance to stress corrosion cracking, Good resistance to pitting and crevice corrosion, High resistance to general corrosion, High resistance to erosion corrosion and corrosion fatigue. PREN ≥ 28 | |
Heat Treatment | Solution annealing at 1020 – 1100°C followed by water quenching | |
Welding | Very good |