Dimension
Property | Value |
---|---|
Length | 3000 - 6000 mm Show Supplier Material materials with Length of 3000 - 6000 mm |
Thickness | 2 - 50 mm Show Supplier Material materials with Thickness of 2 - 50 mm |
Width | 1500 - 2000 mm Show Supplier Material materials with Width of 1500 - 2000 mm |
Mechanical
Property | Temperature | Value |
---|---|---|
Charpy impact energy, V-notch | -46.0 °C | 45 J Show Supplier Material materials with Charpy impact energy, V-notch of 45 J |
Elongation | 23.0 °C | 25 % Show Supplier Material materials with Elongation of 25 % |
Hardness, Brinell | 23.0 °C | 310 [-] Show Supplier Material materials with Hardness, Brinell of 310 [-] |
Tensile strength | 23.0 °C | 750 - 1000 MPa Show Supplier Material materials with Tensile strength of 750 - 1000 MPa |
Yield strength Rp0.2 | 23.0 °C | 550 MPa Show Supplier Material materials with Yield strength Rp0.2 of 550 MPa |
Chemical properties
Property | Value |
---|---|
Carbon | 0.03 % Show Supplier Material materials with Carbon of 0.03 % |
Chromium | 24 - 26 % Show Supplier Material materials with Chromium of 24 - 26 % |
Copper | 0.5 % Show Supplier Material materials with Copper of 0.5 % |
Iron | Balance |
Manganese | 1.2 % Show Supplier Material materials with Manganese of 1.2 % |
Molybdenum | 3 - 5 % Show Supplier Material materials with Molybdenum of 3 - 5 % |
Nickel | 6 - 8 % Show Supplier Material materials with Nickel of 6 - 8 % |
Nitrogen | 0.24 - 0.32 % Show Supplier Material materials with Nitrogen of 0.24 - 0.32 % |
Phosphorus | 0.04 % Show Supplier Material materials with Phosphorus of 0.04 % |
Silicon | 0.8 % Show Supplier Material materials with Silicon of 0.8 % |
Sulfur | 0.02 % Show Supplier Material materials with Sulfur of 0.02 % |
Technological properties
Property | ||
---|---|---|
Application areas | It is widely used in oil & gas, hydropower, pressure vessels, pulp & paper, structural components and chemical tankers. | |
Corrosion properties | High resistance to stress corrosion cracking in halide containing environments, High resistance to pitting and crevice corrosion, High resistance to general corrosion, High resistance to erosion corrosion and corrosion fatigue. PREN ≥ 41 | |
Heat Treatment | Solution annealing at 1100°C followed by water quenching. | |
Welding | Very good |