ALLOY 718 Bar

Alternative and trade names
ALLOY 718, UNS N07718
Want to keep this datasheet? Save it now in your required format

Description

Alloy 718 is a age-hardened nickel-chromium alloy containing also significant amounts of iron, niobium and molybdenum along with lesser amounts of aluminum and titanium. This provides a high strength alloy combined with corrosion resistance. Service temperatures range from -250°C to about 650°C. This alloy has also very good weldability.

Related Standards

Equivalent Materials

This material data has been provided by Sverdrup Steel.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

Dimension

PropertyValue

Diameter

12.7 - 304.8 mm

Show Supplier Material materials with Diameter of 12.7 - 304.8 mm

Mechanical

PropertyTemperatureValue

Charpy impact energy, V-notch

-101.0 °C

27 J

Show Supplier Material materials with Charpy impact energy, V-notch of 27 J

Elongation

23.0 °C

30 %

Show Supplier Material materials with Elongation of 30 %

Hardness, Brinell

23.0 °C

248 - 363 [-]

Show Supplier Material materials with Hardness, Brinell of 248 - 363 [-]

Tensile strength

23.0 °C

895 - 1250 MPa

Show Supplier Material materials with Tensile strength of 895 - 1250 MPa

Yield strength Rp0.2

23.0 °C

725 - 1000 MPa

Show Supplier Material materials with Yield strength Rp0.2 of 725 - 1000 MPa

Chemical properties

PropertyValueComment

Aluminium

0.2 - 0.8 %

Show Supplier Material materials with Aluminium of 0.2 - 0.8 %

Carbon

0.08 %

Show Supplier Material materials with Carbon of 0.08 %

Chromium

17 - 21 %

Show Supplier Material materials with Chromium of 17 - 21 %

Copper

0.3 %

Show Supplier Material materials with Copper of 0.3 %

Manganese

0.35 %

Show Supplier Material materials with Manganese of 0.35 %

Molybdenum

2.8 - 3.3 %

Show Supplier Material materials with Molybdenum of 2.8 - 3.3 %

Nickel

50 - 55 %

Show Supplier Material materials with Nickel of 50 - 55 %

Other

4.75 - 5.5 %

Show Supplier Material materials with Other of 4.75 - 5.5 %

Nb+Ta

Phosphorus

0.02 %

Show Supplier Material materials with Phosphorus of 0.02 %

Silicon

0.35 %

Show Supplier Material materials with Silicon of 0.35 %

Sulfur

0.015 %

Show Supplier Material materials with Sulfur of 0.015 %

Titanium

0.65 - 1.05 %

Show Supplier Material materials with Titanium of 0.65 - 1.05 %

Technological properties

Property
Application areas

Used in pumps, tooling, gas turbines rocket motors and nuclear reactors.

Heat Treatment

Solution annealed at 1000 – 1052°C. Age hardening at 774 – 802°C.

Welding

Very good