General
Property | Value | Comment |
---|---|---|
Bio-based content | 100.0 % Show Supplier Material materials with Bio-based content of 100.0 % | ASTM D6866, EN 16785-1 |
Density | 1.24 g/cm³ Show Supplier Material materials with Density of 1.24 g/cm³ | Literature value |
Residual monomer | 0.5 mg/kg Show Supplier Material materials with Residual monomer of 0.5 mg/kg | Total Corbion PLA method |
Water content | 0.04 % Show Supplier Material materials with Water content of 0.04 % | max., Coulometric Karl-Fischer |
Mechanical
Property | Value | Comment |
---|---|---|
Elastic modulus | 3.5 GPa Show Supplier Material materials with Elastic modulus of 3.5 GPa | ISO 527-1 |
Elongation | 5.0 Show Supplier Material materials with Elongation of 5.0 | ISO 527-1 |
Impact strength, Charpy notched | 5.0 Show Supplier Material materials with Impact strength, Charpy notched of 5.0 | ISO 179-1eA |
Tensile strength | 50.0 MPa Show Supplier Material materials with Tensile strength of 50.0 MPa | ISO 527-1 |
Thermal
Rheological Properties
Property | Value | Comment |
---|---|---|
Melt mass-flow rate | 23.0 g/10min Show Supplier Material materials with Melt mass-flow rate of 23.0 g/10min | ISO 1133-A @ 210°C/2.16kg, 10 g/10 min @ 190°C/2.16kg |
Technological properties
Property | ||
---|---|---|
Application areas | PLA extruded filament for FDM/FFF 3D printing, single-serve capsules for coffee machine, injection molded serviceware, food serviceware | |
Certifications | FOOD CONTACT STATUS: In the European Union, Luminy® PDLA polymers are compliant with EU commission regulation 10/2011 of 14 January 2011 (and amendments) on plastic materials and articles intended to come into contact with food. Lactic acid is considered a dual use substance, since lactic acid is approved as a food additive (additive number E270). There are no SMLs or SML(T)s for the ingredients used to produce Luminy® PDLA. The regulation does include an migration limit of 10 mg/dm2 on the overall migration from finished plastic articles into food. It is the responsibility of the manufacturer of the final product, when intended as a food contact product, to determine that the use of the product is safe and also suitable for the intended application. While it is Total Corbion PLA’s conclusion that the above mentioned polymers are permitted, it is the final product which must meet the given regulations and the manufacturer should take responsibility to check if the final product is in compliance with these regulations. | |
Color | Crystalline White | |
Other | NOTICE REGARDING USE RESTRICTIONS: Unless specifically agreed to in writing, Total Corbion PLA will not knowingly market any product into any of the following commercial or developmental applications: | |
Processing methods | It is recommended to be in contact with a Total Corbion PLA processing expert to discuss exact processing options. MOISTURE & PRE-DRYING: It is recommended to dry Luminy® D120 from the packaging for 4-6 hours at 100°C. Drying of semicrystalline PLA homopolymer can be performed in a desiccant hot air dryer, with a dew point of -40°C or less. It is recommended to reduce the moisture content before melt processing to a level less than 250ppm and preferably less than 100 ppm, measured by e.g. Karl-Fischer or Brabender aquatrac method. Predrying is in particular important prior to injection molding, film and sheet production. Moisture causes hydrolysis of the PLA homopolymer during melt processing, resulting in reduced mechanical performance in the final part. |