General
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Density | 20.0 °C | 4.45 g/cm³ Show Material materials with Density of 4.45 g/cm³ | Annealed | DIN 17851, DIN 17864, DIN 17862, DIN 17860 | Forging, Rod |
Mechanical
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Elastic modulus | 20.0 °C | 116.0 GPa Show Material materials with Elastic modulus of 116.0 GPa | Annealed | DIN 17851, DIN 17864, DIN 17862, DIN 17860 | Forging, Rod | |
Elongation | 20.0 °C | 8.0 Show Material materials with Elongation of 8.0 | Annealed | DIN 17851, DIN 17864, DIN 17862, DIN 17860 | Forging | Transverse |
20.0 °C | 8.0 Show Material materials with Elongation of 8.0 | Annealed | DIN 17862, DIN 17851, DIN 17864, DIN 17860 | Rod | ||
Hardness, Brinell | 20.0 °C | 310.0 Show Material materials with Hardness, Brinell of 310.0 | Annealed | DIN 17862, DIN 17851, DIN 17864, DIN 17860 | Rod | |
Reduction of area | 20.0 °C | 30.0 % Show Material materials with Reduction of area of 30.0 % | Annealed | DIN 17851, DIN 17864, DIN 17862, DIN 17860 | Forging | Transverse |
20.0 °C | 30.0 % Show Material materials with Reduction of area of 30.0 % | Annealed | DIN 17851, DIN 17864, DIN 17862, DIN 17860 | Forging, Rod | ||
Tensile strength | 20.0 °C | 860.0 MPa Show Material materials with Tensile strength of 860.0 MPa | Annealed | DIN 17851, DIN 17864, DIN 17862, DIN 17860 | Forging | Transverse |
20.0 °C | 860.0 MPa Show Material materials with Tensile strength of 860.0 MPa | Annealed | DIN 17851, DIN 17864, DIN 17862, DIN 17860 | Forging, Rod | ||
20.0 °C | 1020.0 MPa Show Material materials with Tensile strength of 1020.0 MPa | Annealed | DIN 17851, DIN 17864, DIN 17862, DIN 17860 | |||
100.0 °C | 925.0 MPa Show Material materials with Tensile strength of 925.0 MPa | Annealed | DIN 17851, DIN 17864, DIN 17862, DIN 17860 | |||
200.0 °C | 840.0 MPa Show Material materials with Tensile strength of 840.0 MPa | Annealed | DIN 17851, DIN 17864, DIN 17862, DIN 17860 | |||
300.0 °C | 770.0 MPa Show Material materials with Tensile strength of 770.0 MPa | Annealed | DIN 17851, DIN 17864, DIN 17862, DIN 17860 | |||
400.0 °C | 715.0 MPa Show Material materials with Tensile strength of 715.0 MPa | Annealed | DIN 17851, DIN 17864, DIN 17862, DIN 17860 | |||
500.0 °C | 585.0 MPa Show Material materials with Tensile strength of 585.0 MPa | Annealed | DIN 17851, DIN 17864, DIN 17862, DIN 17860 |
Thermal
Property | Value | Comment |
---|---|---|
Coefficient of thermal expansion | 7.699999999999999e-06 - 1e-05 1/K Show Material materials with Coefficient of thermal expansion of 7.699999999999999e-06 - 1e-05 1/K | Typical for Titanium Alpha Beta Alloy |
Melting point | 1500.0 - 1750.0 °C Show Material materials with Melting point of 1500.0 - 1750.0 °C | Typical for Titanium Alpha Beta Alloy |
Specific heat capacity | 370.0 - 674.0 J/(kg·K) Show Material materials with Specific heat capacity of 370.0 - 674.0 J/(kg·K) | Typical for Titanium Alpha Beta Alloy |
Thermal conductivity | 6.0 - 12.0 W/(m·K) Show Material materials with Thermal conductivity of 6.0 - 12.0 W/(m·K) | Typical for Titanium Alpha Beta Alloy |
Chemical properties
Property | Value | Condition | Related Standards | Shape |
---|---|---|---|---|
Aluminium | 4.5 - 5.5 % Show Material materials with Aluminium of 4.5 - 5.5 % | Annealed | DIN 17851, DIN 17864, DIN 17862, DIN 17860 | Forging, Rod |
Carbon | 0.08 Show Material materials with Carbon of 0.08 | Annealed | DIN 17851, DIN 17864, DIN 17862, DIN 17860 | Forging, Rod |
Hydrogen | 0.015 Show Material materials with Hydrogen of 0.015 | Annealed | DIN 17851, DIN 17864, DIN 17862, DIN 17860 | Forging, Rod |
Iron | 2.0 - 3.0 % Show Material materials with Iron of 2.0 - 3.0 % | Annealed | DIN 17851, DIN 17864, DIN 17862, DIN 17860 | Forging, Rod |
Nitrogen | 0.05 Show Material materials with Nitrogen of 0.05 | Annealed | DIN 17851, DIN 17864, DIN 17862, DIN 17860 | Forging, Rod |
Oxygen | 0.2 Show Material materials with Oxygen of 0.2 | Annealed | DIN 17851, DIN 17864, DIN 17862, DIN 17860 | Forging, Rod |
Titanium | 90.8 % Show Material materials with Titanium of 90.8 % | Annealed | DIN 17851, DIN 17864, DIN 17862, DIN 17860 | Forging, Rod |