General
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Density | 20.0 °C | 4.55 g/cm³ Show Material materials with Density of 4.55 g/cm³ | Artificially Aged | DIN 17851, DIN 17862, DIN 17864 | Forging |
Mechanical
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Elastic modulus | 20.0 °C | 114.0 GPa Show Material materials with Elastic modulus of 114.0 GPa | Artificially Aged | DIN 17851, DIN 17862, DIN 17864 | Forging |
200.0 °C | 104.0 GPa Show Material materials with Elastic modulus of 104.0 GPa | Artificially Aged | DIN 17851, DIN 17862, DIN 17864 | Forging | |
400.0 °C | 93.0 GPa Show Material materials with Elastic modulus of 93.0 GPa | Artificially Aged | DIN 17851, DIN 17862, DIN 17864 | Forging | |
Elongation | 20.0 °C | 8.0 % Show Material materials with Elongation of 8.0 % | Artificially Aged | DIN 17851, DIN 17864, DIN 17862 | Forging, Rod |
Reduction of area | 20.0 °C | 20.0 % Show Material materials with Reduction of area of 20.0 % | Artificially Aged | DIN 17851, DIN 17864, DIN 17862 | Forging, Rod |
Shear modulus | 20.0 °C | 43.0 GPa Show Material materials with Shear modulus of 43.0 GPa | Artificially Aged | DIN 17851, DIN 17862, DIN 17864 | Forging |
Tensile strength | 20.0 °C | 890.0 MPa Show Material materials with Tensile strength of 890.0 MPa | Artificially Aged | DIN 17851, DIN 17864, DIN 17862 | Forging |
20.0 °C | 920.0 MPa Show Material materials with Tensile strength of 920.0 MPa | Artificially Aged | DIN 17851, DIN 17864, DIN 17862 | Rod | |
20.0 °C | 1030.0 MPa Show Material materials with Tensile strength of 1030.0 MPa | Artificially Aged | DIN 17851, DIN 17864, DIN 17862 | ||
100.0 °C | 945.0 MPa Show Material materials with Tensile strength of 945.0 MPa | Artificially Aged | DIN 17851, DIN 17864, DIN 17862 | ||
200.0 °C | 885.0 MPa Show Material materials with Tensile strength of 885.0 MPa | Artificially Aged | DIN 17851, DIN 17864, DIN 17862 | ||
300.0 °C | 845.0 MPa Show Material materials with Tensile strength of 845.0 MPa | Artificially Aged | DIN 17851, DIN 17864, DIN 17862 | ||
400.0 °C | 785.0 MPa Show Material materials with Tensile strength of 785.0 MPa | Artificially Aged | DIN 17851, DIN 17864, DIN 17862 | ||
500.0 °C | 735.0 MPa Show Material materials with Tensile strength of 735.0 MPa | Artificially Aged | DIN 17851, DIN 17864, DIN 17862 |
Thermal
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Coefficient of thermal expansion | 7.699999999999999e-06 - 1e-05 1/K Show Material materials with Coefficient of thermal expansion of 7.699999999999999e-06 - 1e-05 1/K | Typical for Titanium Alpha Beta Alloy | ||||
Melting point | 1500.0 - 1750.0 °C Show Material materials with Melting point of 1500.0 - 1750.0 °C | Typical for Titanium Alpha Beta Alloy | ||||
Specific heat capacity | 370.0 - 674.0 J/(kg·K) Show Material materials with Specific heat capacity of 370.0 - 674.0 J/(kg·K) | Typical for Titanium Alpha Beta Alloy | ||||
Thermal conductivity | 20.0 °C | 5.86 W/(m·K) Show Material materials with Thermal conductivity of 5.86 W/(m·K) | Artificially Aged | DIN 17851, DIN 17862, DIN 17864 | Forging |
Electrical
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Electrical resistivity | 20.0 °C | 1.91e-06 Ω·m Show Material materials with Electrical resistivity of 1.91e-06 Ω·m | Artificially Aged | DIN 17851, DIN 17862, DIN 17864 | Forging |
Chemical properties
Property | Value | Condition | Related Standards | Shape |
---|---|---|---|---|
Aluminium | 5.5 - 6.5 % Show Material materials with Aluminium of 5.5 - 6.5 % | Artificially Aged | DIN 17851, DIN 17864, DIN 17862 | Forging, Rod |
Carbon | 0.05 Show Material materials with Carbon of 0.05 | Artificially Aged | DIN 17851, DIN 17864, DIN 17862 | Forging, Rod |
Hydrogen | 0.015 Show Material materials with Hydrogen of 0.015 | Artificially Aged | DIN 17851, DIN 17864, DIN 17862 | Forging, Rod |
Iron | 0.25 Show Material materials with Iron of 0.25 | Artificially Aged | DIN 17851, DIN 17864, DIN 17862 | Forging, Rod |
Molybdenum | 1.8 - 2.2 % Show Material materials with Molybdenum of 1.8 - 2.2 % | Artificially Aged | DIN 17851, DIN 17864, DIN 17862 | Forging, Rod |
Nitrogen | 0.05 Show Material materials with Nitrogen of 0.05 | Artificially Aged | DIN 17851, DIN 17864, DIN 17862 | Forging, Rod |
Oxygen | 0.15 Show Material materials with Oxygen of 0.15 | Artificially Aged | DIN 17851, DIN 17864, DIN 17862 | Forging, Rod |
Silicon | 0.06 - 0.12 % Show Material materials with Silicon of 0.06 - 0.12 % | Artificially Aged | DIN 17851, DIN 17864, DIN 17862 | Forging, Rod |
Tin | 1.8 - 2.2 % Show Material materials with Tin of 1.8 - 2.2 % | Artificially Aged | DIN 17851, DIN 17864, DIN 17862 | Forging, Rod |
Titanium | 83.7 % Show Material materials with Titanium of 83.7 % | Artificially Aged | DIN 17851, DIN 17864, DIN 17862 | Forging, Rod |
Zirconium | 3.6 - 4.4 % Show Material materials with Zirconium of 3.6 - 4.4 % | Artificially Aged | DIN 17851, DIN 17864, DIN 17862 | Forging, Rod |