General
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Density | 20.0 °C | 4.54 g/cm³ Show Material materials with Density of 4.54 g/cm³ | Artificially Aged | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Forging, Rod |
Mechanical
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Elastic modulus | 20.0 °C | 116.0 GPa Show Material materials with Elastic modulus of 116.0 GPa | Artificially Aged | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Forging, Rod |
200.0 °C | 108.0 GPa Show Material materials with Elastic modulus of 108.0 GPa | Artificially Aged | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Forging, Rod | |
400.0 °C | 99.0 GPa Show Material materials with Elastic modulus of 99.0 GPa | Artificially Aged | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Forging, Rod | |
Elongation | 20.0 °C | 5.0 % Show Material materials with Elongation of 5.0 % | Artificially Aged | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Forging |
20.0 °C | 6.0 % Show Material materials with Elongation of 6.0 % | Artificially Aged | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Rod | |
Reduction of area | 20.0 °C | 10.0 % Show Material materials with Reduction of area of 10.0 % | Artificially Aged | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Forging |
20.0 °C | 15.0 % Show Material materials with Reduction of area of 15.0 % | Artificially Aged | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Rod | |
Shear modulus | 20.0 °C | 45.0 GPa Show Material materials with Shear modulus of 45.0 GPa | Artificially Aged | WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860 | Rod |
Tensile strength | 20.0 °C | 1100.0 MPa Show Material materials with Tensile strength of 1100.0 MPa | Artificially Aged | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Forging |
20.0 °C | 1200.0 MPa Show Material materials with Tensile strength of 1200.0 MPa | Artificially Aged | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Rod | |
20.0 °C | 1315.0 MPa Show Material materials with Tensile strength of 1315.0 MPa | Artificially Aged | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | ||
100.0 °C | 1225.0 MPa Show Material materials with Tensile strength of 1225.0 MPa | Artificially Aged | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | ||
200.0 °C | 1110.0 MPa Show Material materials with Tensile strength of 1110.0 MPa | Artificially Aged | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | ||
300.0 °C | 1000.0 MPa Show Material materials with Tensile strength of 1000.0 MPa | Artificially Aged | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | ||
400.0 °C | 785.0 MPa Show Material materials with Tensile strength of 785.0 MPa | Artificially Aged | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 |
Thermal
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Coefficient of thermal expansion | 7.699999999999999e-06 - 1e-05 1/K Show Material materials with Coefficient of thermal expansion of 7.699999999999999e-06 - 1e-05 1/K | Typical for Titanium Alpha Beta Alloy | ||||
Melting point | 1500.0 - 1750.0 °C Show Material materials with Melting point of 1500.0 - 1750.0 °C | Typical for Titanium Alpha Beta Alloy | ||||
Specific heat capacity | 370.0 - 674.0 J/(kg·K) Show Material materials with Specific heat capacity of 370.0 - 674.0 J/(kg·K) | Typical for Titanium Alpha Beta Alloy | ||||
Thermal conductivity | 20.0 °C | 6.5 W/(m·K) Show Material materials with Thermal conductivity of 6.5 W/(m·K) | Artificially Aged | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Forging, Rod |
Electrical
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Electrical resistivity | 20.0 °C | 1.57e-06 Ω·m Show Material materials with Electrical resistivity of 1.57e-06 Ω·m | Artificially Aged | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Forging, Rod |
Chemical properties
Property | Value | Condition | Related Standards | Shape |
---|---|---|---|---|
Aluminium | 5.0 - 6.0 % Show Material materials with Aluminium of 5.0 - 6.0 % | Artificially Aged | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Forging, Rod |
Carbon | 0.05 Show Material materials with Carbon of 0.05 | Artificially Aged | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Forging, Rod |
Copper | 0.35 - 1.0 % Show Material materials with Copper of 0.35 - 1.0 % | Artificially Aged | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Forging, Rod |
Hydrogen | 0.015 Show Material materials with Hydrogen of 0.015 | Artificially Aged | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Forging, Rod |
Iron | 0.35 - 1.0 % Show Material materials with Iron of 0.35 - 1.0 % | Artificially Aged | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Forging, Rod |
Nitrogen | 0.04 Show Material materials with Nitrogen of 0.04 | Artificially Aged | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Forging, Rod |
Oxygen | 0.2 Show Material materials with Oxygen of 0.2 | Artificially Aged | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Forging, Rod |
Tin | 1.5 - 2.5 % Show Material materials with Tin of 1.5 - 2.5 % | Artificially Aged | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Forging, Rod |
Titanium | 82.8 % Show Material materials with Titanium of 82.8 % | Artificially Aged | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Forging, Rod |
Vanadium | 5.0 - 6.0 % Show Material materials with Vanadium of 5.0 - 6.0 % | Artificially Aged | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Forging, Rod |