General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 21.4 g/cm³ Show Material materials with Density of 21.4 g/cm³ | Typical for Platinum |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 20.0 °C | 212 GPa Show Material materials with Elastic modulus of 212 GPa | |
Elongation | 20.0 °C | 1 % Show Material materials with Elongation of 1 % | |
Hardness, Vickers | 20.0 °C | 463 [-] Show Material materials with Hardness, Vickers of 463 [-] | |
Poisson's ratio | 23.0 °C | 0.39 [-] Show Material materials with Poisson's ratio of 0.39 [-] | Typical for Platinum |
Shear modulus | 23.0 °C | 62 GPa Show Material materials with Shear modulus of 62 GPa | Typical for Platinum |
Tensile strength | 20.0 °C | 1617 MPa Show Material materials with Tensile strength of 1617 MPa | |
Yield strength Rp0.2 | 20.0 °C | 1605 MPa Show Material materials with Yield strength Rp0.2 of 1605 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 8.8E-6 - 9.1E-6 1/K Show Material materials with Coefficient of thermal expansion of 8.8E-6 - 9.1E-6 1/K | Typical for Platinum |
Melting point | 1769 °C Show Material materials with Melting point of 1769 °C | Typical for Platinum | |
Specific heat capacity | 23.0 °C | 136 J/(kg·K) Show Material materials with Specific heat capacity of 136 J/(kg·K) | Typical for Platinum |
Thermal conductivity | 23.0 °C | 69 - 73 W/(m·K) Show Material materials with Thermal conductivity of 69 - 73 W/(m·K) | Typical for Platinum |