General
Property | Temperature | Value |
---|---|---|
Density | 20.0 °C | 20 g/cm³ Show Material materials with Density of 20 g/cm³ |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 20.0 °C | 208 GPa Show Material materials with Elastic modulus of 208 GPa | |
Elongation | 20.0 °C | 32 % Show Material materials with Elongation of 32 % | |
Hardness, Vickers | 20.0 °C | 102 [-] Show Material materials with Hardness, Vickers of 102 [-] | |
Poisson's ratio | 23.0 °C | 0.39 [-] Show Material materials with Poisson's ratio of 0.39 [-] | Typical for Platinum |
Shear modulus | 20.0 °C | 72 GPa Show Material materials with Shear modulus of 72 GPa | |
Tensile strength | 20.0 °C | 300 MPa Show Material materials with Tensile strength of 300 MPa | |
Yield strength | 20.0 °C | 180 MPa Show Material materials with Yield strength of 180 MPa | |
Yield strength Rp0.2 | 20.0 °C | 180 MPa Show Material materials with Yield strength Rp0.2 of 180 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 300.0 °C | 1.02E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.02E-5 1/K | |
700.0 °C | 1.07E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.07E-5 1/K | ||
1200.0 °C | 1.12E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.12E-5 1/K | ||
Melting point | 1769 °C Show Material materials with Melting point of 1769 °C | Typical for Platinum | |
Specific heat capacity | 23.0 °C | 136 J/(kg·K) Show Material materials with Specific heat capacity of 136 J/(kg·K) | Typical for Platinum |
Thermal conductivity | 20.0 °C | 30 W/(m·K) Show Material materials with Thermal conductivity of 30 W/(m·K) |
Electrical
Property | Temperature | Value |
---|---|---|
Electrical resistivity | 20.0 °C | 2E-7 Ω·m Show Material materials with Electrical resistivity of 2E-7 Ω·m |
Chemical properties