Properties
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 21.4 g/cm³ Show Material materials with Density of 21.4 g/cm³ | Typical for Platinum |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 154 - 172 GPa Show Material materials with Elastic modulus of 154 - 172 GPa | Typical for Platinum |
Elongation | 20.0 °C | 44 % Show Material materials with Elongation of 44 % | |
200.0 °C | 40 % Show Material materials with Elongation of 40 % | ||
300.0 °C | 37 % Show Material materials with Elongation of 37 % | ||
400.0 °C | 40 % Show Material materials with Elongation of 40 % | ||
500.0 °C | 42 % Show Material materials with Elongation of 42 % | ||
600.0 °C | 44 % Show Material materials with Elongation of 44 % | ||
700.0 °C | 46 % Show Material materials with Elongation of 46 % | ||
900.0 °C | 56 % Show Material materials with Elongation of 56 % | ||
1100.0 °C | 63 % Show Material materials with Elongation of 63 % | ||
1250.0 °C | 71 % Show Material materials with Elongation of 71 % | ||
1500.0 °C | 67 % Show Material materials with Elongation of 67 % | ||
Poisson's ratio | 23.0 °C | 0.39 [-] Show Material materials with Poisson's ratio of 0.39 [-] | Typical for Platinum |
Reduction of area | 20.0 °C | 98 % Show Material materials with Reduction of area of 98 % | |
300.0 °C | 98 % Show Material materials with Reduction of area of 98 % | ||
500.0 °C | 98 % Show Material materials with Reduction of area of 98 % | ||
700.0 °C | 98 % Show Material materials with Reduction of area of 98 % | ||
900.0 °C | 98 % Show Material materials with Reduction of area of 98 % | ||
1100.0 °C | 94 % Show Material materials with Reduction of area of 94 % | ||
1250.0 °C | 99 % Show Material materials with Reduction of area of 99 % | ||
1500.0 °C | 99 % Show Material materials with Reduction of area of 99 % | ||
Shear modulus | 23.0 °C | 62 GPa Show Material materials with Shear modulus of 62 GPa | Typical for Platinum |
Tensile strength | 20.0 °C | 221 - 225 MPa Show Material materials with Tensile strength of 221 - 225 MPa | |
200.0 °C | 190 MPa Show Material materials with Tensile strength of 190 MPa | ||
300.0 °C | 170 MPa Show Material materials with Tensile strength of 170 MPa | ||
400.0 °C | 150 MPa Show Material materials with Tensile strength of 150 MPa | ||
500.0 °C | 135 - 138 MPa Show Material materials with Tensile strength of 135 - 138 MPa | ||
600.0 °C | 120 MPa Show Material materials with Tensile strength of 120 MPa | ||
700.0 °C | 101 - 103 MPa Show Material materials with Tensile strength of 101 - 103 MPa | ||
900.0 °C | 70 MPa Show Material materials with Tensile strength of 70 MPa | ||
1100.0 °C | 42 MPa Show Material materials with Tensile strength of 42 MPa | ||
1250.0 °C | 30 MPa Show Material materials with Tensile strength of 30 MPa | ||
1500.0 °C | 16 MPa Show Material materials with Tensile strength of 16 MPa | ||
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 8.8E-6 - 9.1E-6 1/K Show Material materials with Coefficient of thermal expansion of 8.8E-6 - 9.1E-6 1/K | Typical for Platinum |
Melting point | 1769 °C Show Material materials with Melting point of 1769 °C | Typical for Platinum | |
Specific heat capacity | 23.0 °C | 136 J/(kg·K) Show Material materials with Specific heat capacity of 136 J/(kg·K) | Typical for Platinum |
Thermal conductivity | 20.0 °C | 33 W/(m·K) Show Material materials with Thermal conductivity of 33 W/(m·K) |
Chemical properties