Eigenschaften
Allgemein
| Property | Temperature | Value |
|---|---|---|
Dichte | 23.0 °C | 7.45 g/cm³ Show Supplier Material materials with Dichte of 7.45 g/cm³ |
Recycled Content | 80 % Show Supplier Material materials with Recycled Content of 80 % |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dauerfestigkeit | 23.0 °C | 255 MPa Show Supplier Material materials with Dauerfestigkeit of 255 MPa | 100.000.000 cycles |
Dehnung A5 | 23.0 °C | 6 % Show Supplier Material materials with Dehnung A5 of 6 % | |
Druckfestigkeit | 23.0 °C | 1241 MPa Show Supplier Material materials with Druckfestigkeit of 1241 MPa | |
Druckfestigkeit, 0,1% | 23.0 °C | 758 MPa Show Supplier Material materials with Druckfestigkeit, 0,1% of 758 MPa | |
Elastizitätsmodul | 23.0 °C | 124 GPa Show Supplier Material materials with Elastizitätsmodul of 124 GPa | |
Flächenreduzierung | 23.0 °C | 5 % Show Supplier Material materials with Flächenreduzierung of 5 % | |
Härte, HBW | 23.0 °C | 293 [-] Show Supplier Material materials with Härte, HBW of 293 [-] | HBW 10/3000 |
Härte, Rockwell C | 23.0 °C | 30 [-] Show Supplier Material materials with Härte, Rockwell C of 30 [-] | |
Kerbschlagenergie | 23.0 °C | 6.8 J Show Supplier Material materials with Kerbschlagenergie of 6.8 J | |
Scherfestigkeit | 23.0 °C | 552 MPa Show Supplier Material materials with Scherfestigkeit of 552 MPa | |
Streckgrenze Rp0,5 | 23.0 °C | 724 MPa Show Supplier Material materials with Streckgrenze Rp0,5 of 724 MPa | |
Zugfestigkeit | 23.0 °C | 930 MPa Show Supplier Material materials with Zugfestigkeit of 930 MPa |
Thermisch
| Property | Temperature | Value |
|---|---|---|
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.6E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.6E-5 1/K |
Spezifische Wärmekapazität | 23.0 °C | 450 J/(kg·K) Show Supplier Material materials with Spezifische Wärmekapazität of 450 J/(kg·K) |
Wärmeleitfähigkeit | 23.0 °C | 42 W/(m·K) Show Supplier Material materials with Wärmeleitfähigkeit of 42 W/(m·K) |
Elektrisch
| Property | Temperature | Value |
|---|---|---|
Elektrische Leitfähigkeit | 23.0 °C | 4.80E+6 S/m Show Supplier Material materials with Elektrische Leitfähigkeit of 4.80E+6 S/m |
Specific Electrical conductivity | 8.2 % IACS Show Supplier Material materials with Specific Electrical conductivity of 8.2 % IACS |
Chemical properties
| Property | Value |
|---|---|
Aluminium | 10.5 % Show Supplier Material materials with Aluminium of 10.5 % |
Andere | 0.5 % Show Supplier Material materials with Andere of 0.5 % |
Eisen | 4.8 % Show Supplier Material materials with Eisen of 4.8 % |
Kupfer | Balance |
Mangan | 1.5 % Show Supplier Material materials with Mangan of 1.5 % |
Nickel | 5 % Show Supplier Material materials with Nickel of 5 % |
Technological properties
| Property | ||
|---|---|---|
| Application areas | AMPCO® M4 was initially developed as an aircraft specification alloy for gears in retractable landing assemblies, engine spacer bearings and other similar applications. It is rapidly growing in use where higher mechanical properties at elevated temperatures together with corrosion-resistant properties are required. Typical applications include aircraft landing gear bearings and bushings, bending dies (shoes and mandrels) for the tube bending industry, gear wheels and wear/guide plates, etc.. | |