Eigenschaften
Allgemein
| Property | Value |
|---|---|
Recycled Content | 80 % Show Supplier Material materials with Recycled Content of 80 % |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dehnung | 23.0 °C | 40 % Show Supplier Material materials with Dehnung of 40 % | in 2″ (51 mm) |
Härte, Brinell | 23.0 °C | 80 [-] Show Supplier Material materials with Härte, Brinell of 80 [-] | BHN (500 kg) 1/4″ deposit |
Zugfestigkeit | 23.0 °C | 350 MPa Show Supplier Material materials with Zugfestigkeit of 350 MPa |
Chemical properties
| Property | Value | Comment | |
|---|---|---|---|
Aluminium | 0.01 % Show Supplier Material materials with Aluminium of 0.01 % | max. | |
Andere | 0.5 % Show Supplier Material materials with Andere of 0.5 % | max. | |
Blei | 0.02 % Show Supplier Material materials with Blei of 0.02 % | max. | |
Eisen | 0.5 % Show Supplier Material materials with Eisen of 0.5 % | max. | |
Kupfer | Balance, including silver | ||
Mangan | 1.5 % Show Supplier Material materials with Mangan of 1.5 % | max. | |
Silizium | 2.8 - 4 % Show Supplier Material materials with Silizium of 2.8 - 4 % | ||
Zink | 1 % Show Supplier Material materials with Zink of 1 % | max. | |
Zinn | 1 % Show Supplier Material materials with Zinn of 1 % | max. | |
Technological properties
| Property | ||
|---|---|---|
| Processing methods | Welding Procedure: With gas metal-arc welding, the weld metal should be deposited in stringer beads, maintaining a small molten pool to avoid overheating the hot short silicon bronze base metal. Use argon gas for shielding and relatively high welding travel speeds. With the gas-tungsten arc welding process, welding is accomplished with dcen current and argon or helium gas shielding. ACHF with argon gas shielding may be used to take advantage of the arc cleaning action. Preheat: Preheat slightly to remove moisture. Interpass temperature should not exceed 150°F (66°C). | |