Eigenschaften
Allgemein
| Property | Value |
|---|---|
Dichte | 6.5 g/cm³ Show Supplier Material materials with Dichte of 6.5 g/cm³ |
Kornstruktur | Titanium carbide + martensite |
Mechanisch
| Property | Value |
|---|---|
Biegefestigkeit | 1200 MPa Show Supplier Material materials with Biegefestigkeit of 1200 MPa |
Druckfestigkeit | 3600 MPa Show Supplier Material materials with Druckfestigkeit of 3600 MPa |
Elastizitätsmodul | 294 GPa Show Supplier Material materials with Elastizitätsmodul of 294 GPa |
Härte, Rockwell C | 69 [-] Show Supplier Material materials with Härte, Rockwell C of 69 [-] |
Schubmodule | 122 GPa Show Supplier Material materials with Schubmodule of 122 GPa |
Thermisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 100 °C | 1.06e-05 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.06e-05 1/K | for 20°C to the mentioned temperature |
200 °C | 1.16e-05 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.16e-05 1/K | for 20°C to the mentioned temperature | |
300 °C | 1.22e-05 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.22e-05 1/K | for 20°C to the mentioned temperature | |
400 °C | 1.24e-05 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.24e-05 1/K | for 20°C to the mentioned temperature | |
500 °C | 1.27e-05 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.27e-05 1/K | for 20°C to the mentioned temperature | |
600 °C | 1.29e-05 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.29e-05 1/K | for 20°C to the mentioned temperature | |
Wärmeleitfähigkeit | 18.2 W/(m·K) Show Supplier Material materials with Wärmeleitfähigkeit of 18.2 W/(m·K) |
Elektrisch
| Property | Value |
|---|---|
spezifischer Widerstand | 9.1e-07 Ω·m Show Supplier Material materials with spezifischer Widerstand of 9.1e-07 Ω·m |
Magnetisch
Chemical properties
| Property | Value | Comment | |
|---|---|---|---|
Andere | 33 % Show Supplier Material materials with Andere of 33 % | TiC | |
Chrom | 13.5 % Show Supplier Material materials with Chrom of 13.5 % | ||
Eisen | Balance | ||
Kohlenstoff | 0.75 % Show Supplier Material materials with Kohlenstoff of 0.75 % | ||
Molybdän | 3 % Show Supplier Material materials with Molybdän of 3 % | ||
Technological properties
| Property | ||
|---|---|---|
| Application areas | In heat-treated, hardened condition (up to 69 HRC), Ferro-Titanit® can be used to solve many wear problems economically. | |
| General machinability | In as-delivered condition, this material can be machined by conventional methods. | |
| Heat Treatment | Soft annealing: 750°C, 10 hr (Cooling in furnace) Hardness: 51 HRC - Stress-relief-annealing: 600-650°C (cooling in Furnace) - Hardening: 1080°C and quenching in vacuum (1 bar N2) - Temepering 460°C (Hardness:69 HRC) | |