Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Bio-based content | 100 % Show Supplier Material materials with Bio-based content of 100 % | ||
Dichte | 23.0 °C | 1.23 g/cm³ Show Supplier Material materials with Dichte of 1.23 g/cm³ | ISO 2781 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 43 MPa Show Supplier Material materials with Biegefestigkeit of 43 MPa | ISO 527 |
Biegemodul | 23.0 °C | 3.2 GPa Show Supplier Material materials with Biegemodul of 3.2 GPa | ISO 527 |
Zugfestigkeit | 23.0 °C | 40 MPa Show Supplier Material materials with Zugfestigkeit of 40 MPa | ISO 527 |
Thermisch
Property | Value | Comment |
---|---|---|
Schmelzpunkt | 150 - 170 °C Show Supplier Material materials with Schmelzpunkt of 150 - 170 °C | |
Vicat-Erweichungstemperatur | 48 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 48 °C | ISO 306 |
Rheological Properties
Property | Value | Comment |
---|---|---|
Schmelzmassenflussrate | 22 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 22 g/10min | ISO 1133 |
Technological properties
Property | ||
---|---|---|
Application areas | This material contains wood fibres, and imitates wood in terms of its smell and aesthetic. | |
Chemical composition | Biodegradable batch based on PLA, contains copolyester and additives. | |
Handling recommendations | Store at room temperature (18-27°C / 65-80°F), out of direct heat and sunlight, and in a dry place. When stored correctly, this material has a shelf life of 1 year |