Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.21 g/cm³ Show Material materials with Dichte of 1.21 g/cm³ | ISO 1183 |
Wasserabsorption | 23.0 °C | 6.5 % Show Material materials with Wasserabsorption of 6.5 % | Sim. to ISO 62 | 80mil |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 160 MPa Show Material materials with Biegefestigkeit of 160 MPa | ISO 178 |
Biegemodul | 23.0 °C | 4.7 GPa Show Material materials with Biegemodul of 4.7 GPa | ISO 178 |
Dehnung | 23.0 °C | 4 % Show Material materials with Dehnung of 4 % | ISO 527-1/-2 |
Elastizitätsmodul | 23.0 °C | 5.1 GPa Show Material materials with Elastizitätsmodul of 5.1 GPa | ISO 527-1/-2 |
Hardness, Ball Indentation | 23.0 °C | 180 MPa Show Material materials with Hardness, Ball Indentation of 180 MPa | ISO 2039-1 |
Hardness, Rockwell R | 23.0 °C | 120 [-] Show Material materials with Hardness, Rockwell R of 120 [-] | ISO 2039-2 |
Härte, Rockwell M | 23.0 °C | 90 [-] Show Material materials with Härte, Rockwell M of 90 [-] | ISO 2039-2 |
Poissonzahl | 23.0 °C | 0.35 [-] Show Material materials with Poissonzahl of 0.35 [-] | |
Schlagfestigkeit, Charpy gekerbt | -6.0 °C | 6 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 6 kJ/m² | ISO 179/1eA |
23.0 °C | 8 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 8 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | -6.0 °C | 59 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 59 kJ/m² | ISO 179/1eU |
23.0 °C | 67 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 67 kJ/m² | ISO 179/1eU | |
Schlagzähigkeit, Izod ungekerbt | -30.0 °C | 6 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 6 kJ/m² | ISO 180/1A |
23.0 °C | 8 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 8 kJ/m² | ISO 180/1A | |
Zugfestigkeit | 23.0 °C | 118 MPa Show Material materials with Zugfestigkeit of 118 MPa | ISO 527-1/-2 |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 260 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 260 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 242 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 242 °C | ISO 75-1/-2 | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 5E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 5E-5 1/K | ISO 11359-1/-2 | ||
Relative temperature index, electrical | 90 °C Show Material materials with Relative temperature index, electrical of 90 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 65 °C Show Material materials with Relative temperature index, mechanical impact of 65 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 90 °C Show Material materials with Relative temperature index, mechanical strength of 90 °C | UL 746B | 120mil | |||
Schmelzpunkt | 263 °C Show Material materials with Schmelzpunkt of 263 °C | ISO 11357-1/-3 | 18°F/min | |||
Spezifische Wärmekapazität | 23.0 °C | 2140 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 2140 J/(kg·K) | of melt | ||
Temperaturleitfähigkeit | 23.0 °C | 0 mm²/s Show Material materials with Temperaturleitfähigkeit of 0 mm²/s | |||
Vicat-Erweichungstemperatur | 240 °C Show Material materials with Vicat-Erweichungstemperatur of 240 °C | ISO 306 | 90°F/h, 11 lbf | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 1.3E-4 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 1.3E-4 1/K | ISO 11359-1/-2 | ||
Entflammbarkeit | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.75 mm, UL recognition: yes -, Glow Wire Flammability Index, 40mil: 650 °C, Glow Wire Flammability Index, 80mil: 650 °C, Glow Wire Flammability Index, 120mil: 650 °C, Glow Wire Ignition Temperature, 40mil: 650 °C, Glow Wire Ignition Temperature, 80mil: 650 °C, Glow Wire Ignition Temperature, 120mil: 650 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: 19 mm/min |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dielektrizitätskonstante, 1 MHz | 23.0 °C | 3.7 [-] Show Material materials with Dielektrizitätskonstante, 1 MHz of 3.7 [-] | IEC 62631-2-1 |
Dielektrizitätskonstante, 100 Hz | 23.0 °C | 3.9 [-] Show Material materials with Dielektrizitätskonstante, 100 Hz of 3.9 [-] | IEC 62631-2-1 |
Dissipation factor, 100Hz | 23.0 °C | 6.5E-3 [-] Show Material materials with Dissipation factor, 100Hz of 6.5E-3 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.01 [-] Show Material materials with Dissipation factor, 1MHz of 0.01 [-] | IEC 62631-2-1 |
Durchschlagfestigkeit | 23.0 °C | 37 kV/mm Show Material materials with Durchschlagfestigkeit of 37 kV/mm | IEC 60243-1 |
Kriechstromfestigkeit | 23.0 °C | 475 V Show Material materials with Kriechstromfestigkeit of 475 V | IEC 60112 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 13% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 295°C, Min. melt temperature: 285°C, Max. melt temperature: 305°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 80°C, Min. mold temperature: 50°C, Max. mold temperature: 100°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C |