Propiedades
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Densidad | 2.82 g/cm³ Show Material materials with Densidad of 2.82 g/cm³ | T6 | EN 573-3, EN 755 |
2.83 g/cm³ Show Material materials with Densidad of 2.83 g/cm³ | T6 | EN 573-3, EN 755 |
Mecánica
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Bending Fatigue Strength | 125.0 MPa Show Material materials with Bending Fatigue Strength of 125.0 MPa | T6 | EN 573-3, EN 755 | |
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 2000 Series Aluminium | ||
Módulo de cizallamiento | 27.3 GPa Show Material materials with Módulo de cizallamiento of 27.3 GPa | T6 | EN 573-3, EN 755 | |
Módulo elástico | 70.0 GPa Show Material materials with Módulo elástico of 70.0 GPa | T6 | EN 573-3, EN 755 | |
72.5 GPa Show Material materials with Módulo elástico of 72.5 GPa | T6 | EN 573-3, EN 755 | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | ||
Resistencia a la tracción | 295.0 MPa Show Material materials with Resistencia a la tracción of 295.0 MPa | T6 | EN 573-3, EN 755 | |
310.0 MPa Show Material materials with Resistencia a la tracción of 310.0 MPa | T6 | EN 573-3, EN 755 |
Aplicaciones térmicas
| Property | Temperature | Value | Condition | Related Standards |
|---|---|---|---|---|
Calor específico | 864.0 J/(kg·K) Show Material materials with Calor específico of 864.0 J/(kg·K) | T6 | EN 573-3, EN 755 | |
Coeficiente de dilatación térmica | -50 °C | 2.14e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.14e-05 1/K | T6 | EN 573-3, EN 755 |
20 °C | 2.14e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.14e-05 1/K | T6 | EN 573-3, EN 755 | |
20 °C | 2.2899999999999998e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.2899999999999998e-05 1/K | T6 | EN 573-3, EN 755 | |
20 °C | 2.3399999999999996e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3399999999999996e-05 1/K | T6 | EN 573-3, EN 755 | |
20 °C | 2.4e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.4e-05 1/K | T6 | EN 573-3, EN 755 | |
20 °C | 2.4999999999999998e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.4999999999999998e-05 1/K | T6 | EN 573-3, EN 755 | |
100 °C | 2.2899999999999998e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.2899999999999998e-05 1/K | T6 | EN 573-3, EN 755 | |
100 °C | 2.3399999999999996e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3399999999999996e-05 1/K | T6 | EN 573-3, EN 755 | |
200 °C | 2.4e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.4e-05 1/K | T6 | EN 573-3, EN 755 | |
300 °C | 2.4999999999999998e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.4999999999999998e-05 1/K | T6 | EN 573-3, EN 755 | |
Conductividad térmica | 151.0 - 172.0 W/(m·K) Show Material materials with Conductividad térmica of 151.0 - 172.0 W/(m·K) | T6 | EN 573-3, EN 755 | |
170.0 - 220.0 W/(m·K) Show Material materials with Conductividad térmica of 170.0 - 220.0 W/(m·K) | T6 | EN 573-3, EN 755 | ||
Temperatura de fusión | 540.0 - 645.0 °C Show Material materials with Temperatura de fusión of 540.0 - 645.0 °C | T6 | EN 573-3, EN 755 | |
585.0 - 650.0 °C Show Material materials with Temperatura de fusión of 585.0 - 650.0 °C | T6 | EN 573-3, EN 755 |
Eléctrico
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Conductividad eléctrica | 23000000.0 - 26000000.0 S/m Show Material materials with Conductividad eléctrica of 23000000.0 - 26000000.0 S/m | T6 | EN 573-3, EN 755 |
24000000.0 - 32000000.0 S/m Show Material materials with Conductividad eléctrica of 24000000.0 - 32000000.0 S/m | T6 | EN 573-3, EN 755 | |
Resistividad eléctrica | 3.13e-08 - 4.17e-08 Ω·m Show Material materials with Resistividad eléctrica of 3.13e-08 - 4.17e-08 Ω·m | T6 | EN 573-3, EN 755 |
3.85e-08 - 4.35e-08 Ω·m Show Material materials with Resistividad eléctrica of 3.85e-08 - 4.35e-08 Ω·m | T6 | EN 573-3, EN 755 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Bismuto | 0.2 - 0.8 % Show Material materials with Bismuto of 0.2 - 0.8 % | T6 | EN 573-3, EN 755 |
Cobre | 5.0 - 6.0 % Show Material materials with Cobre of 5.0 - 6.0 % | T6 | EN 573-3, EN 755 |
Hierro | 0.70 % Show Material materials with Hierro of 0.70 % | T6 | EN 573-3, EN 755 |
Plomo | 0.2 - 0.6 % Show Material materials with Plomo of 0.2 - 0.6 % | T6 | EN 573-3, EN 755 |
Silicona | 0.4 % Show Material materials with Silicona of 0.4 % | T6 | EN 573-3, EN 755 |
Zinc | 0.3 % Show Material materials with Zinc of 0.3 % | T6 | EN 573-3, EN 755 |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | decorative: not suitable, Protective: poor | |
| Brazing | hard brazing (with flux/ without flux): not suitable /, friction soldering: sufficient | |
| Corrosion properties | Seawater: poor, weathering: sufficient | |
| Workability | Deep drawing / upsetting (Condition) - / acceptable | |