General
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Dureza Brinell (HBW) | 23.0 °C | 285 [-] Show Supplier Material materials with Dureza Brinell (HBW) of 285 [-] | HBW 10/3000 |
Dureza Rockwell C | 23.0 °C | 29 [-] Show Supplier Material materials with Dureza Rockwell C of 29 [-] | |
Elongación A5 | 23.0 °C | 1.5 % Show Supplier Material materials with Elongación A5 of 1.5 % | |
Energía de impacto Charpy | 23.0 °C | 2.7 J Show Supplier Material materials with Energía de impacto Charpy of 2.7 J | |
Energía de impacto Izod | 23.0 °C | 2.7 J Show Supplier Material materials with Energía de impacto Izod of 2.7 J | |
Estricción | 23.0 °C | 0.5 % Show Supplier Material materials with Estricción of 0.5 % | |
Límite elástico Rp0.5 | 23.0 °C | 379 MPa Show Supplier Material materials with Límite elástico Rp0.5 of 379 MPa | |
Límite elástico a la compresión, 0,1% | 23.0 °C | 483 MPa Show Supplier Material materials with Límite elástico a la compresión, 0,1% of 483 MPa | |
Módulo elástico | 23.0 °C | 103 GPa Show Supplier Material materials with Módulo elástico of 103 GPa | |
Resistencia a la compresión | 23.0 °C | 1310 MPa Show Supplier Material materials with Resistencia a la compresión of 1310 MPa | |
Resistencia a la tracción | 23.0 °C | 552 MPa Show Supplier Material materials with Resistencia a la tracción of 552 MPa | |
Resistencia al cizallamiento | 23.0 °C | 448 MPa Show Supplier Material materials with Resistencia al cizallamiento of 448 MPa |
Aplicaciones térmicas
Property | Temperature | Value |
---|---|---|
Calor específico | 23.0 °C | 420 J/(kg·K) Show Supplier Material materials with Calor específico of 420 J/(kg·K) |
Coeficiente de dilatación térmica | 23.0 °C | 1.62E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.62E-5 1/K |
Conductividad térmica | 23.0 °C | 42 W/(m·K) Show Supplier Material materials with Conductividad térmica of 42 W/(m·K) |
Eléctrico
Property | Temperature | Value |
---|---|---|
Conductividad eléctrica | 23.0 °C | 6.00E+6 S/m Show Supplier Material materials with Conductividad eléctrica of 6.00E+6 S/m |
Specific Electrical conductivity | 10 % IACS Show Supplier Material materials with Specific Electrical conductivity of 10 % IACS |
Chemical properties
Technological properties
Property | ||
---|---|---|
Application areas | AMPCO® 21 is used for guide port bushings and wear strips replacing hardened steel and for some cams when no impact is involved. However, the largest single use is as die rings, inserts, forming rolls, etc. in forming, bending or drawing operations, especially when stainless steel is the material being processed. AMPCO® 21 is also widely used as work support blades for the centerless grinding of steel rods. |