Property | Temperature | Value |
---|---|---|
Dureza Brinell (HBW) | 23.0 °C | 290 [-] Show Supplier Material materials with Dureza Brinell (HBW) of 290 [-] |
Dureza Rockwell C | 23.0 °C | 31 [-] Show Supplier Material materials with Dureza Rockwell C of 31 [-] |
Elongación | 23.0 °C | 25 % Show Supplier Material materials with Elongación of 25 % |
Resistencia a la tracción | 23.0 °C | 750 MPa Show Supplier Material materials with Resistencia a la tracción of 750 MPa |
Chemical properties
Property | Value |
---|---|
Azufre | 0.01 % Show Supplier Material materials with Azufre of 0.01 % |
Carbono | 0.03 % Show Supplier Material materials with Carbono of 0.03 % |
Cobre | 0.5 - 1 % Show Supplier Material materials with Cobre of 0.5 - 1 % |
Cromo | 24 - 26 % Show Supplier Material materials with Cromo of 24 - 26 % |
Fósforo | 0.03 % Show Supplier Material materials with Fósforo of 0.03 % |
Hierro | Balance |
Manganeso | 1 % Show Supplier Material materials with Manganeso of 1 % |
Molibdeno | 3 - 4 % Show Supplier Material materials with Molibdeno of 3 - 4 % |
Nitrógeno | 0.2 - 0.3 % Show Supplier Material materials with Nitrógeno of 0.2 - 0.3 % |
Níquel | 6 - 8 % Show Supplier Material materials with Níquel of 6 - 8 % |
Silicona | 1 % Show Supplier Material materials with Silicona of 1 % |
Wolframio | 0.5 - 1 % Show Supplier Material materials with Wolframio of 0.5 - 1 % |
Technological properties
Property | ||
---|---|---|
Corrosion properties | Stress Corrosion: material is tested in accordance with ASTM G48 (Method A) (latest version). The test piece will be taken from the same location as those for mechanical testing. Acceptance is that no pitting is to be observed at 20x magnification after exposure for 24 hours at 50 degrees C. Weight loss will not exceed 4.0 g/mm2. Method and results are reported. |