General
Property | Value |
---|---|
Densidad | 7.9 g/cm³ Show Supplier Material materials with Densidad of 7.9 g/cm³ |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Dureza Brinell | 223 [-] Show Supplier Material materials with Dureza Brinell of 223 [-] | ||
Elongación | 30 % Show Supplier Material materials with Elongación of 30 % | A5 | |
Límite elástico | 20 °C | 250 MPa Show Supplier Material materials with Límite elástico of 250 MPa | RP02 |
20 °C | 500 MPa Show Supplier Material materials with Límite elástico of 500 MPa | 460 | |
100 °C | 460 MPa Show Supplier Material materials with Límite elástico of 460 MPa | RP02 | |
200 °C | 185 MPa Show Supplier Material materials with Límite elástico of 185 MPa | RP02 | |
200 °C | 450 MPa Show Supplier Material materials with Límite elástico of 450 MPa | RP1 | |
300 °C | 180 MPa Show Supplier Material materials with Límite elástico of 180 MPa | RP02 | |
300 °C | 445 MPa Show Supplier Material materials with Límite elástico of 445 MPa | RP1 | |
400 °C | 175 MPa Show Supplier Material materials with Límite elástico of 175 MPa | RP02 | |
400 °C | 430 MPa Show Supplier Material materials with Límite elástico of 430 MPa | RP1 | |
500 °C | 170 MPa Show Supplier Material materials with Límite elástico of 170 MPa | RP02 | |
500 °C | 415 MPa Show Supplier Material materials with Límite elástico of 415 MPa | RP1 | |
600 °C | 165 MPa Show Supplier Material materials with Límite elástico of 165 MPa | RP02 | |
600 °C | 340 MPa Show Supplier Material materials with Límite elástico of 340 MPa | RP1 | |
700 °C | 150 MPa Show Supplier Material materials with Límite elástico of 150 MPa | RP02 | |
700 °C | 250 MPa Show Supplier Material materials with Límite elástico of 250 MPa | RP1 | |
Módulo elástico | 200 GPa Show Supplier Material materials with Módulo elástico of 200 GPa | ||
Resistencia a la tracción | 550 - 750 MPa Show Supplier Material materials with Resistencia a la tracción of 550 - 750 MPa |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Calor específico | 500 J/(kg·K) Show Supplier Material materials with Calor específico of 500 J/(kg·K) | ||
Coeficiente de dilatación térmica | 200 °C | 1.65e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.65e-05 1/K | for 20°C to the mentioned temperature |
400 °C | 1.75e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.75e-05 1/K | for 20°C to the mentioned temperature | |
600 °C | 1.8e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.8e-05 1/K | for 20°C to the mentioned temperature | |
800 °C | 1.85e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.85e-05 1/K | for 20°C to the mentioned temperature | |
1000 °C | 1.95e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.95e-05 1/K | for 20°C to the mentioned temperature | |
Conductividad térmica | 15 W/(m·K) Show Supplier Material materials with Conductividad térmica of 15 W/(m·K) | ||
500 °C | 21 W/(m·K) Show Supplier Material materials with Conductividad térmica of 21 W/(m·K) |
Eléctrico
Property | Value |
---|---|
Resistividad eléctrica | 8.5e-07 Ω·m Show Supplier Material materials with Resistividad eléctrica of 8.5e-07 Ω·m |
Chemical properties
Property | Value |
---|---|
Azufre | 0.015 % Show Supplier Material materials with Azufre of 0.015 % |
Carbono | 0.2 % Show Supplier Material materials with Carbono of 0.2 % |
Cromo | 19 - 21 % Show Supplier Material materials with Cromo of 19 - 21 % |
Fósforo | 0.045 % Show Supplier Material materials with Fósforo of 0.045 % |
Hierro | Balance |
Níquel | 11 - 13 % Show Supplier Material materials with Níquel of 11 - 13 % |
Silicona | 1.5 - 2 % Show Supplier Material materials with Silicona of 1.5 - 2 % |
Technological properties
Property | ||
---|---|---|
Application areas | Construction of high temperature components, Automotive engineering, Chains, screens and mesh, Mechanical engineering, Furnace engineering | |
Corrosion properties | FERROTHERM® 4828 is only slightly resistant to both oxidising and reducing sulphurous gases. In these media the use of FERROTHERM® 4828 is limited to temperatures below 650 °C. The corrosion resistance to carbonizing (up to 900 °C) as well as to nitrogenous, oxygen-poor gases is to be classified as medium. | |
General machinability | Good - The formation of carbides in 1.4828 will result in increased wear of cutting tools. In addition to this, rapid work hardening and poor thermal conductivity require the use of adequate cooling and good quality cutting/machining tools. | |
Heat Treatment | Optimal material properties are realised after solution annealing in the temperature range 1050 - 1150°C followed by rapid cooling in air or water. During operation and fabrication, the time spent in the temperature range 550 - 900°C must be minimised to avoid embrittlement, both chromium carbide precipitation and sigma phase formation. This embrittlement effect can be reversed by solution annealing the steel at a temperature in the range 1050 to 1100°C. | |
Processing history | Solution Annealed | |
Welding | Good - 1.4828 is weldable using all usual welding processes with no preheating being required. Low heat inputs should be used when welding, and post weld heat treatment is not necessary. Novonit 4829 and 4842 are suitable for use as filler materials when welding 1.4828. |