General
Property | Value |
---|---|
Densidad | 7.7 g/cm³ Show Supplier Material materials with Densidad of 7.7 g/cm³ |
Medidas
Property | Value | Comment |
---|---|---|
Diámetro | 160 mm Show Supplier Material materials with Diámetro of 160 mm | max. |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Charpy impact energy, V-notch | 12 J Show Supplier Material materials with Charpy impact energy, V-notch of 12 J | ||
Dureza Brinell | 245 [-] Show Supplier Material materials with Dureza Brinell of 245 [-] | annealed | |
Dureza Rockwell C | 55 [-] Show Supplier Material materials with Dureza Rockwell C of 55 [-] | ||
Elongación | 10 % Show Supplier Material materials with Elongación of 10 % | A5 | |
Módulo elástico | 20 °C | 215 GPa Show Supplier Material materials with Módulo elástico of 215 GPa | |
100 °C | 212 GPa Show Supplier Material materials with Módulo elástico of 212 GPa | ||
200 °C | 205 GPa Show Supplier Material materials with Módulo elástico of 205 GPa | ||
300 °C | 200 GPa Show Supplier Material materials with Módulo elástico of 200 GPa | ||
400 °C | 190 GPa Show Supplier Material materials with Módulo elástico of 190 GPa | ||
Resistencia a la tracción | 800 - 1000 MPa Show Supplier Material materials with Resistencia a la tracción of 800 - 1000 MPa |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Calor específico | 460 J/(kg·K) Show Supplier Material materials with Calor específico of 460 J/(kg·K) | ||
Coeficiente de dilatación térmica | 100 °C | 1.05e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.05e-05 1/K | for 20°C to the mentioned temperature |
200 °C | 1.1e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.1e-05 1/K | for 20°C to the mentioned temperature | |
300 °C | 1.15e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.15e-05 1/K | for 20°C to the mentioned temperature | |
400 °C | 1.2e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.2e-05 1/K | for 20°C to the mentioned temperature | |
Conductividad térmica | 30 W/(m·K) Show Supplier Material materials with Conductividad térmica of 30 W/(m·K) |
Eléctrico
Property | Value |
---|---|
Resistividad eléctrica | 5.5e-07 Ω·m Show Supplier Material materials with Resistividad eléctrica of 5.5e-07 Ω·m |
Chemical properties
Property | Value |
---|---|
Azufre | 0.03 % Show Supplier Material materials with Azufre of 0.03 % |
Carbono | 0.43 - 0.5 % Show Supplier Material materials with Carbono of 0.43 - 0.5 % |
Cromo | 12.5 - 14 % Show Supplier Material materials with Cromo of 12.5 - 14 % |
Fósforo | 0.04 % Show Supplier Material materials with Fósforo of 0.04 % |
Hierro | Balance |
Manganeso | 1 % Show Supplier Material materials with Manganeso of 1 % |
Níquel | 1 % Show Supplier Material materials with Níquel of 1 % |
Silicona | 1 % Show Supplier Material materials with Silicona of 1 % |
Technological properties
Property | ||
---|---|---|
Application areas | Medical and Pharmaceutical industry, Roller Bearings, Mechanical Engineering, Cutlery, Blade and Tool Industry | |
Corrosion properties | Average - Good corrosion resistance in moderately corrosive environments that are free of chlorides, such as soaps, detergents and organic acids. Good resistance to water and steam. 1.4034 is not resistant to intergranular corrosion in the as-delivered or as-welded conditions. Due to the precipitation of chromium carbides and the formation of chromium depleted regions adjacent to these precipitates, 1.4034 should not be used in the soft annealed or over tempered conditions if corrosion resistance is an issue. Optimal corrosion resistance is thus achieved in the hardened condition with a polished surface finish. PRE = 12.5 – 14.5 | |
General machinability | Poor - The machinability of this grade of stainless steel is directly related to its hardness. 1.4034 machines similar to carbon steels of the same hardness. Although it must be realised that the machining parameters will vary depending on the structure/hardness of the steel. | |
Heat Treatment | 1.4034 can be soft annealed by holding at a temperature in the range 750 °C to 850 °C followed by slow cooling in an oven or in air. This steel may be hardened by heating to 1050 °C followed by rapid cooling in air or oil. After hardening and stress relieving at 200 °C. | |
Hot forming | It is formable at 800-1100°C | |
Processing history | Quenched and tempered QT 800 | |
Welding | Poor - Although 1.4034 is generally not welded, it is soldered in some instances. |