Propiedades
General
| Property | Value |
|---|---|
Densidad relativa | 8.89 [-] Show Supplier Material materials with Densidad relativa of 8.89 [-] |
Mecánica
| Property | Value | Comment |
|---|---|---|
Dureza Vickers | 60 - 120 [-] Show Supplier Material materials with Dureza Vickers of 60 - 120 [-] | 1/4H Temper | for thickness 0.15-5 mm |
90 - 155 [-] Show Supplier Material materials with Dureza Vickers of 90 - 155 [-] | 1/2H Temper | for thickness 0.1-5 mm | |
120 - 165 [-] Show Supplier Material materials with Dureza Vickers of 120 - 165 [-] | H Temper | for thickness 0.1-5 mm | |
140 [-] Show Supplier Material materials with Dureza Vickers of 140 [-] | min. | EH Temper | for thickness 0.05-5 mm | |
Elongación | 3 % Show Supplier Material materials with Elongación of 3 % | min. | H Temper | for thickness 0.1-5 mm |
10 % Show Supplier Material materials with Elongación of 10 % | min. | 1/2H Temper | for thickness 0.1-5 mm | |
30 % Show Supplier Material materials with Elongación of 30 % | min. | 1/4H Temper | for thickness 0.1-5 mm | |
40 % Show Supplier Material materials with Elongación of 40 % | min. | O Temper | for thickness 0.1-5 mm | |
Módulo de flexión | 100 GPa Show Supplier Material materials with Módulo de flexión of 100 GPa | |
Módulo elástico | 110 GPa Show Supplier Material materials with Módulo elástico of 110 GPa | |
Plegabilidad 90 ° bidireccional | 0 [-] Show Supplier Material materials with Plegabilidad 90 ° bidireccional of 0 [-] | O Temper | Ts=280 N/mm2 |
0 [-] Show Supplier Material materials with Plegabilidad 90 ° bidireccional of 0 [-] | 1/4H Temper | Ts=298 N/mm2 | |
1 [-] Show Supplier Material materials with Plegabilidad 90 ° bidireccional of 1 [-] | 1/2H Temper | Ts=354 N/mm2 | |
1.5 [-] Show Supplier Material materials with Plegabilidad 90 ° bidireccional of 1.5 [-] | H Temper | Ts=409 N/mm2 | |
2 [-] Show Supplier Material materials with Plegabilidad 90 ° bidireccional of 2 [-] | EH Temper | Ts=484 N/mm2 | |
Plegabilidad 90 ° en peso bruto | 0 [-] Show Supplier Material materials with Plegabilidad 90 ° en peso bruto of 0 [-] | O Temper | Ts=280 N/mm2 |
0 [-] Show Supplier Material materials with Plegabilidad 90 ° en peso bruto of 0 [-] | 1/4H Temper | Ts=298 N/mm2 | |
0 [-] Show Supplier Material materials with Plegabilidad 90 ° en peso bruto of 0 [-] | 1/2H Temper | Ts=354 N/mm2 | |
0 [-] Show Supplier Material materials with Plegabilidad 90 ° en peso bruto of 0 [-] | H Temper | Ts=409 N/mm2 | |
1.3 [-] Show Supplier Material materials with Plegabilidad 90 ° en peso bruto of 1.3 [-] | EH Temper | Ts=484 N/mm2 | |
Resistencia a la tracción | 240 MPa Show Supplier Material materials with Resistencia a la tracción of 240 MPa | min. | O Temper | for thickness 0.1-5 mm |
240 - 330 MPa Show Supplier Material materials with Resistencia a la tracción of 240 - 330 MPa | 1/4H Temper | for thickness 0.1-5 mm | |
330 - 450 MPa Show Supplier Material materials with Resistencia a la tracción of 330 - 450 MPa | 1/2H Temper | for thickness 0.1-5 mm | |
390 - 500 MPa Show Supplier Material materials with Resistencia a la tracción of 390 - 500 MPa | H Temper | for thickness 0.1-5 mm | |
460 MPa Show Supplier Material materials with Resistencia a la tracción of 460 MPa | min. | EH Temper | for thickness 0.1-5 mm |
Aplicaciones térmicas
| Property | Value |
|---|---|
Coeficiente de dilatación térmica | 1.78e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.78e-05 1/K |
Conductividad térmica | 205 W/(m·K) Show Supplier Material materials with Conductividad térmica of 205 W/(m·K) |
Temperatura de fusión | 1075 °C Show Supplier Material materials with Temperatura de fusión of 1075 °C |
Eléctrico
| Property | Value |
|---|---|
Specific Electrical conductivity | 40 % IACS Show Supplier Material materials with Specific Electrical conductivity of 40 % IACS |
Chemical properties
| Property | Value | Comment |
|---|---|---|
Estaño | 1 - 1.7 % Show Supplier Material materials with Estaño of 1 - 1.7 % | |
Fósforo | 0.15 % Show Supplier Material materials with Fósforo of 0.15 % | max. |
Hierro | 0.1 % Show Supplier Material materials with Hierro of 0.1 % | max. |
Otro | 99.5 % Show Supplier Material materials with Otro of 99.5 % | min. | Cu+Sn+P |
Plomo | 0.02 % Show Supplier Material materials with Plomo of 0.02 % | max. |
Zinc | 0.2 % Show Supplier Material materials with Zinc of 0.2 % | max. |
Technological properties
| Property | ||
|---|---|---|
| Application areas | The grade is particularly suitable for electronics (connectors, lead frames, lead terminals, transistor terminals, etc.), electrical (relay and switch contacts, rotary switch slides and contacts, fuse clips, etc.), automotive (bearing frames, hydraulic equipment caps, packing, bearings, clutch disks, electrical parts, etc.) and others (bellows, slides, blades, plate springs, corrosion-proof machinery equipment, diaphragms, etc.) | |
| Coating | Standard product specification of a HOT-DIP-tinned strip. *Width means the slit width after plating. *Different plating thickness for each side is possible. * We can accommodate our products to individual specifications other than the above standard specifications. Please feel free to call us. | |
| Other | Hardness Vickers note: Minimum test force is 1.961 N | |
| Tolerances | ||