Propiedades
General
| Property | Value |
|---|---|
Densidad relativa | 8.78 [-] Show Supplier Material materials with Densidad relativa of 8.78 [-] |
Mecánica
| Property | Value | Comment |
|---|---|---|
Dureza Vickers | 200 - 240 [-] Show Supplier Material materials with Dureza Vickers of 200 - 240 [-] | H Temper | for thickness 0.1-1.6 mm |
230 - 270 [-] Show Supplier Material materials with Dureza Vickers of 230 - 270 [-] | EH Temper | for thickness 0.1-0.8 mm | |
250 - 300 [-] Show Supplier Material materials with Dureza Vickers of 250 - 300 [-] | SH Temper | for thickness 0.1-0.4 mm | |
270 [-] Show Supplier Material materials with Dureza Vickers of 270 [-] | min. | ESH Temper | for thickness 0.1-0.4 mm | |
290 [-] Show Supplier Material materials with Dureza Vickers of 290 [-] | min. | XSH Temper | for thickness 0.1-0.4 mm | |
Elongación | 5 % Show Supplier Material materials with Elongación of 5 % | min. | SH Temper | for thickness 0.1-0.4 mm |
9 % Show Supplier Material materials with Elongación of 9 % | min. | EH Temper | for thickness 0.1-0.8 mm | |
11 % Show Supplier Material materials with Elongación of 11 % | min. | H Temper | for thickness 0.1-1.6 mm | |
Límite elástico | 430 MPa Show Supplier Material materials with Límite elástico of 430 MPa | min. | H Temper | for spring material (Kb0.1) | for thickness 0.15-1.6 mm |
510 MPa Show Supplier Material materials with Límite elástico of 510 MPa | min. | EH Temper | for spring material (Kb0.1) | for thickness 0.15-1.6 mm | |
510 MPa Show Supplier Material materials with Límite elástico of 510 MPa | min. | H Temper | for thickness 0.1-1.6 mm, RP02 | |
570 MPa Show Supplier Material materials with Límite elástico of 570 MPa | min. | SH Temper | for spring material (Kb0.1) | for thickness 0.15-1.6 mm | |
630 MPa Show Supplier Material materials with Límite elástico of 630 MPa | min. | ESH Temper | for spring material (Kb0.1) | for thickness 0.15-1.6 mm | |
630 MPa Show Supplier Material materials with Límite elástico of 630 MPa | min. | EH Temper | for thickness 0.1-0.8 mm, RP02 | |
700 MPa Show Supplier Material materials with Límite elástico of 700 MPa | min. | XSH Temper | for spring material (Kb0.1) | for thickness 0.15-1.6 mm | |
750 MPa Show Supplier Material materials with Límite elástico of 750 MPa | min. | SH Temper | for thickness 0.1-0.4 mm, RP02 | |
870 MPa Show Supplier Material materials with Límite elástico of 870 MPa | min. | ESH Temper | for thickness 0.1-0.4 mm, RP02 | |
930 MPa Show Supplier Material materials with Límite elástico of 930 MPa | min. | XSH Temper | for thickness 0.1-0.4 mm, RP02 | |
Módulo de flexión | 100 GPa Show Supplier Material materials with Módulo de flexión of 100 GPa | |
Módulo elástico | 105 GPa Show Supplier Material materials with Módulo elástico of 105 GPa | |
Resistencia a la tracción | 650 - 750 MPa Show Supplier Material materials with Resistencia a la tracción of 650 - 750 MPa | H Temper | for thickness 0.1-1.6 mm |
750 - 850 MPa Show Supplier Material materials with Resistencia a la tracción of 750 - 850 MPa | EH Temper | for thickness 0.1-0.8 mm | |
850 - 950 MPa Show Supplier Material materials with Resistencia a la tracción of 850 - 950 MPa | SH Temper | for thickness 0.1-0.4 mm | |
950 MPa Show Supplier Material materials with Resistencia a la tracción of 950 MPa | min. | ESH Temper | for thickness 0.1-0.4 mm | |
1000 MPa Show Supplier Material materials with Resistencia a la tracción of 1000 MPa | min. | XSH Temper | for thickness 0.1-0.4 mm |
Aplicaciones térmicas
| Property | Value |
|---|---|
Calor específico | 375 J/(kg·K) Show Supplier Material materials with Calor específico of 375 J/(kg·K) |
Coeficiente de dilatación térmica | 1.84e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.84e-05 1/K |
Conductividad térmica | 50 W/(m·K) Show Supplier Material materials with Conductividad térmica of 50 W/(m·K) |
Temperatura de fusión | 845 - 1000 °C Show Supplier Material materials with Temperatura de fusión of 845 - 1000 °C |
Eléctrico
| Property | Value |
|---|---|
Specific Electrical conductivity | 10 % IACS Show Supplier Material materials with Specific Electrical conductivity of 10 % IACS |
Chemical properties
| Property | Value | Comment |
|---|---|---|
Estaño | 9 - 11 % Show Supplier Material materials with Estaño of 9 - 11 % | |
Fósforo | 0.03 - 0.35 % Show Supplier Material materials with Fósforo of 0.03 - 0.35 % | |
Hierro | 0.1 % Show Supplier Material materials with Hierro of 0.1 % | max. |
Otro | 99.5 % Show Supplier Material materials with Otro of 99.5 % | min. | Cu+Sn+P |
Plomo | 0.02 % Show Supplier Material materials with Plomo of 0.02 % | max. |
Zinc | 0.2 % Show Supplier Material materials with Zinc of 0.2 % | max. |
Technological properties
| Property | ||
|---|---|---|
| Application areas | The grade is particularly suitable for electronics (connectors, lead frames, lead terminals, transistor terminals, etc.), electrical (relay and switch contacts, rotary switch slides and contacts, fuse clips, etc.), automotive (bearing frames, hydraulic equipment caps, packing, bearings, clutch disks, electrical parts, etc.) and others (bellows, slides, blades, plate springs, corrosion-proof machinery equipment, diaphragms, etc.) | |
| Coating | Standard product specification of a HOT-DIP-tinned strip. *Width means the slit width after plating. *Different plating thickness for each side is possible. * We can accommodate our products to individual specifications other than the above standard specifications. Please feel free to call us. | |
| Other | Hardness Vickers note: Minimum test force is 1.961 N | |
| Tolerances | ||