General
Property | Value |
---|---|
Densidad relativa | 8.87 [-] Show Supplier Material materials with Densidad relativa of 8.87 [-] |
Mecánica
Property | Value | Comment |
---|---|---|
Dureza Vickers | 70 - 115 [-] Show Supplier Material materials with Dureza Vickers of 70 - 115 [-] | O Temper | for thickness 0.1-5 mm |
125 - 165 [-] Show Supplier Material materials with Dureza Vickers of 125 - 165 [-] | 1/2H Temper | for thickness 0.1-5 mm | |
150 - 185 [-] Show Supplier Material materials with Dureza Vickers of 150 - 185 [-] | H Temper | for thickness 0.1-5 mm | |
175 - 205 [-] Show Supplier Material materials with Dureza Vickers of 175 - 205 [-] | EH Temper | for thickness 0.1-5 mm | |
185 - 215 [-] Show Supplier Material materials with Dureza Vickers of 185 - 215 [-] | SH Temper | for thickness 0.1-5 mm | |
Elongación | 2 % Show Supplier Material materials with Elongación of 2 % | min. | EH Temper | for thickness 0.1-5 mm |
5 % Show Supplier Material materials with Elongación of 5 % | min. | H Temper | for thickness 0.1-5 mm | |
10 % Show Supplier Material materials with Elongación of 10 % | min. | 1/2H Temper | for thickness 0.1-5 mm | |
30 % Show Supplier Material materials with Elongación of 30 % | min. | O Temper | for thickness 0.1-5 mm | |
Módulo de flexión | 112 GPa Show Supplier Material materials with Módulo de flexión of 112 GPa | |
Módulo elástico | 122 GPa Show Supplier Material materials with Módulo elástico of 122 GPa | |
Plegabilidad 90 ° bidireccional | 0 [-] Show Supplier Material materials with Plegabilidad 90 ° bidireccional of 0 [-] | O Temper | Ts=331 N/mm2 |
0.5 [-] Show Supplier Material materials with Plegabilidad 90 ° bidireccional of 0.5 [-] | 1/2H Temper | Ts=467 N/mm2 | |
1 [-] Show Supplier Material materials with Plegabilidad 90 ° bidireccional of 1 [-] | H Temper | Ts=515 N/mm2 | |
2.5 [-] Show Supplier Material materials with Plegabilidad 90 ° bidireccional of 2.5 [-] | EH Temper | Ts=572 N/mm2 | |
Plegabilidad 90 ° en peso bruto | 0 [-] Show Supplier Material materials with Plegabilidad 90 ° en peso bruto of 0 [-] | O Temper | Ts=331 N/mm2 |
0 [-] Show Supplier Material materials with Plegabilidad 90 ° en peso bruto of 0 [-] | 1/2H Temper | Ts=467 N/mm2 | |
0.5 [-] Show Supplier Material materials with Plegabilidad 90 ° en peso bruto of 0.5 [-] | H Temper | Ts=515 N/mm2 | |
1 [-] Show Supplier Material materials with Plegabilidad 90 ° en peso bruto of 1 [-] | EH Temper | Ts=572 N/mm2 | |
1.5 [-] Show Supplier Material materials with Plegabilidad 90 ° en peso bruto of 1.5 [-] | SH Temper | Ts=644 N/mm2 | |
Resistencia a la tracción | 300 MPa Show Supplier Material materials with Resistencia a la tracción of 300 MPa | min. | O Temper | for thickness 0.1-5 mm |
400 - 500 MPa Show Supplier Material materials with Resistencia a la tracción of 400 - 500 MPa | 1/2H Temper | for thickness 0.1-5 mm | |
450 - 550 MPa Show Supplier Material materials with Resistencia a la tracción of 450 - 550 MPa | H Temper | for thickness 0.1-5 mm | |
500 - 600 MPa Show Supplier Material materials with Resistencia a la tracción of 500 - 600 MPa | EH Temper | for thickness 0.1-5 mm | |
600 - 700 MPa Show Supplier Material materials with Resistencia a la tracción of 600 - 700 MPa | SH Temper | for thickness 0.1-5 mm |
Aplicaciones térmicas
Property | Value |
---|---|
Coeficiente de dilatación térmica | 1.65e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.65e-05 1/K |
Conductividad térmica | 152 W/(m·K) Show Supplier Material materials with Conductividad térmica of 152 W/(m·K) |
Temperatura de fusión | 1065 °C Show Supplier Material materials with Temperatura de fusión of 1065 °C |
Eléctrico
Property | Value |
---|---|
Specific Electrical conductivity | 32 % IACS Show Supplier Material materials with Specific Electrical conductivity of 32 % IACS |
Chemical properties
Property | Value | Comment |
---|---|---|
Estaño | 1.7 - 2.3 % Show Supplier Material materials with Estaño of 1.7 - 2.3 % | |
Fósforo | 0.15 % Show Supplier Material materials with Fósforo of 0.15 % | max. |
Hierro | 0.1 % Show Supplier Material materials with Hierro of 0.1 % | max. |
Otro | 99.5 % Show Supplier Material materials with Otro of 99.5 % | min. | Cu+Sn+P |
Plomo | 0.02 % Show Supplier Material materials with Plomo of 0.02 % | max. |
Zinc | 0.2 % Show Supplier Material materials with Zinc of 0.2 % | max. |
Technological properties
Property | ||
---|---|---|
Application areas | The grade is particularly suitable for electronics (connectors, lead frames, lead terminals, transistor terminals, etc.), electrical (relay and switch contacts, rotary switch slides and contacts, fuse clips, etc.), automotive (bearing frames, hydraulic equipment caps, packing, bearings, clutch disks, electrical parts, etc.) and others (bellows, slides, blades, plate springs, corrosion-proof machinery equipment, diaphragms, etc.) | |
Coating | Standard product specification of a HOT-DIP-tinned strip. *Width means the slit width after plating. *Different plating thickness for each side is possible. * We can accommodate our products to individual specifications other than the above standard specifications. Please feel free to call us. | |
Other | Hardness Vickers note: Minimum test force is 1.961 N | |
Tolerances |