General
Property | Value |
---|---|
Densidad relativa | 8.86 [-] Show Supplier Material materials with Densidad relativa of 8.86 [-] |
Mecánica
Property | Value | Comment |
---|---|---|
Dureza Vickers | 90 - 160 [-] Show Supplier Material materials with Dureza Vickers of 90 - 160 [-] | 1/4H Temper | for thickness 0.1-5 mm |
130 - 190 [-] Show Supplier Material materials with Dureza Vickers of 130 - 190 [-] | 1/2H Temper | for thickness 0.1-5 mm | |
170 - 220 [-] Show Supplier Material materials with Dureza Vickers of 170 - 220 [-] | H Temper | for thickness 0.1-5 mm | |
190 - 230 [-] Show Supplier Material materials with Dureza Vickers of 190 - 230 [-] | EH Temper | for thickness 0.05-5 mm | |
200 [-] Show Supplier Material materials with Dureza Vickers of 200 [-] | min. | SH Temper | for thickness 0.05-5 mm | |
Elongación | 4 % Show Supplier Material materials with Elongación of 4 % | min. | EH Temper | for thickness 0.2-5 mm |
7 % Show Supplier Material materials with Elongación of 7 % | min. | H Temper | for thickness 0.1-5 mm | |
15 % Show Supplier Material materials with Elongación of 15 % | min. | 1/2H Temper | for thickness 0.1-5 mm | |
28 % Show Supplier Material materials with Elongación of 28 % | min. | 1/4H Temper | for thickness 0.1-5 mm | |
40 % Show Supplier Material materials with Elongación of 40 % | min. | O Temper | for thickness 0.1-5 mm | |
Módulo de flexión | 110 GPa Show Supplier Material materials with Módulo de flexión of 110 GPa | |
Módulo elástico | 115 GPa Show Supplier Material materials with Módulo elástico of 115 GPa | |
Resistencia a la tracción | 305 MPa Show Supplier Material materials with Resistencia a la tracción of 305 MPa | min. | O Temper | for thickness 0.1-5 mm |
375 - 470 MPa Show Supplier Material materials with Resistencia a la tracción of 375 - 470 MPa | 1/4H Temper | for thickness 0.1-5 mm | |
470 - 570 MPa Show Supplier Material materials with Resistencia a la tracción of 470 - 570 MPa | 1/2H Temper | for thickness 0.1-5 mm | |
570 - 665 MPa Show Supplier Material materials with Resistencia a la tracción of 570 - 665 MPa | H Temper | for thickness 0.1-5 mm | |
620 - 710 MPa Show Supplier Material materials with Resistencia a la tracción of 620 - 710 MPa | EH Temper | for thickness 0.1-5 mm | |
660 MPa Show Supplier Material materials with Resistencia a la tracción of 660 MPa | min. | SH Temper | for thickness 0.1-5 mm |
Aplicaciones térmicas
Property | Value |
---|---|
Calor específico | 377 J/(kg·K) Show Supplier Material materials with Calor específico of 377 J/(kg·K) |
Coeficiente de dilatación térmica | 1.78e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.78e-05 1/K |
Conductividad térmica | 71 W/(m·K) Show Supplier Material materials with Conductividad térmica of 71 W/(m·K) |
Temperatura de fusión | 950 - 1050 °C Show Supplier Material materials with Temperatura de fusión of 950 - 1050 °C |
Eléctrico
Property | Value |
---|---|
Specific Electrical conductivity | 17 % IACS Show Supplier Material materials with Specific Electrical conductivity of 17 % IACS |
Chemical properties
Property | Value | Comment |
---|---|---|
Estaño | 4.5 - 5.5 % Show Supplier Material materials with Estaño of 4.5 - 5.5 % | |
Fósforo | 0.03 - 0.35 % Show Supplier Material materials with Fósforo of 0.03 - 0.35 % | |
Hierro | 0.1 % Show Supplier Material materials with Hierro of 0.1 % | max. |
Otro | 99.5 % Show Supplier Material materials with Otro of 99.5 % | min. | Cu+Sn+P |
Plomo | 0.02 % Show Supplier Material materials with Plomo of 0.02 % | max. |
Zinc | 0.2 % Show Supplier Material materials with Zinc of 0.2 % | max. |
Technological properties
Property | ||
---|---|---|
Application areas | The grade is particularly suitable for electronics (connectors, lead frames, lead terminals, transistor terminals, etc.), electrical (relay and switch contacts, rotary switch slides and contacts, fuse clips, etc.), automotive (bearing frames, hydraulic equipment caps, packing, bearings, clutch disks, electrical parts, etc.) and others (bellows, slides, blades, plate springs, corrosion-proof machinery equipment, diaphragms, etc.) | |
Coating | Standard product specification of a HOT-DIP-tinned strip. *Width means the slit width after plating. *Different plating thickness for each side is possible. * We can accommodate our products to individual specifications other than the above standard specifications. Please feel free to call us. | |
Other | Hardness Vickers note: Minimum test force is 1.961 N | |
Tolerances |