Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.07 % Show Material materials with Absorción de agua of 0.07 % | ISO 62 | 23°C, 50% RH |
Densidad | 23.0 °C | 1.19 g/cm³ Show Material materials with Densidad of 1.19 g/cm³ | ASTM D 792 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 102 % Show Material materials with Elongación of 102 % | ASTM D 638 | Type I, 50 mm/min |
Elongation at yield | 23.0 °C | 5.7 % Show Material materials with Elongation at yield of 5.7 % | ASTM D 638 | Type I, 50 mm/min |
Flexural yield strength | 23.0 °C | 92 MPa Show Material materials with Flexural yield strength of 92 MPa | ISO 178 | 2 mm/min |
Impact strength, Izod notched, ASTM | -30.0 °C | 230 J/m Show Material materials with Impact strength, Izod notched, ASTM of 230 J/m | ASTM D 256 |
23.0 °C | 740 J/m Show Material materials with Impact strength, Izod notched, ASTM of 740 J/m | ASTM D 256 | |
Impact strength, Izod unnotched, ASTM | -30.0 °C | 2000 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 2000 J/m | ASTM D 4812 |
23.0 °C | 2150 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 2150 J/m | ASTM D 4812 | |
Límite elástico | 23.0 °C | 56 MPa Show Material materials with Límite elástico of 56 MPa | ASTM D 638 | Type I, 50 mm/min |
Módulo de flexión | 23.0 °C | 2.3 GPa Show Material materials with Módulo de flexión of 2.3 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 2.25 GPa Show Material materials with Módulo elástico of 2.25 GPa | ASTM D 638 | 50 mm/min |
Resistencia a la tracción | 23.0 °C | 51 MPa Show Material materials with Resistencia a la tracción of 51 MPa | ASTM D 638 | Type I, 50 mm/min |
Resistencia al choque, ensayo Charpy entallado | -30.0 °C | 16 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 16 kJ/m² | ISO 179/1eA |
23.0 °C | 50 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 50 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Charpy no entallado | -30.0 °C | 134 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 134 kJ/m² | ISO 179/1eU |
23.0 °C | 135 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 135 kJ/m² | ISO 179/1eU | |
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 21 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 21 kJ/m² | ISO 180/1A |
23.0 °C | 58 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 58 kJ/m² | ISO 180/1A | |
Resistencia al choque, ensayo Izod no entallado | -30.0 °C | 183 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 183 kJ/m² | ISO 180/1U |
23.0 °C | 184 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 184 kJ/m² | ISO 180/1U | |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 6.9E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 6.9E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 7.1E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 7.1E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Heat deflection temperature, 1.80 MPa | 118 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 118 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |||
Temperatura de reblandecimiento Vicat | 136 °C Show Material materials with Temperatura de reblandecimiento Vicat of 136 °C | ASTM D 1525 | Rate B/50 | |||
Inflamabilidad | UL Compliant, 94-5VB Rating | 2mm | UL 94 by SABIC-IP | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Constante dieléctrica | 23.0 °C | 2.8 [-] Show Material materials with Constante dieléctrica of 2.8 [-] | SABIC method | at 10 GHz |
Factor de disipación | 23.0 °C | 5.2E-3 [-] Show Material materials with Factor de disipación of 5.2E-3 [-] | SABIC method | at 10 GHz |
Volume resistivity | 23.0 °C | 1.00E+16 - 1.00E+17 Ω·cm Show Material materials with Volume resistivity of 1.00E+16 - 1.00E+17 Ω·cm | ASTM D 257 |
Índice de seguimiento comparativo | 23.0 °C | 3 V Show Material materials with Índice de seguimiento comparativo of 3 V | UL 746A |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.6 - 0.8 % Show Material materials with Contracción of 0.6 - 0.8 % | SABIC method | 3.2 mm |
Contracción transversal | 23.0 °C | 0.6 - 0.8 % Show Material materials with Contracción transversal of 0.6 - 0.8 % | SABIC method |
Velocidad de flujo de la masa derretida | 30 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 30 g/10min | ASTM D 1238 | 300°C/1.2 kg | |
Velocidad de flujo del volumen derretido | 29 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 29 cm³/10min | ISO 1133 | 300°C/1.2 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | ATM/Ticket Machine,Audio,Circuit Protection,Data Transfer,Displays,Enclosure/Housing/Cover,Enclosures,EV Infrastructure,LED Lighting,Non-LED Lighting,Personal Computing,Power Manangement,Wireless Communications | |
| Processing methods | Drying Temperature: 120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 48hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 270-295°C, Nozzle Temperature: 265-290°C, Front - Zone 3 Temperature: 270-295°C, Middle - Zone 2 Temperature: 260-280°C, Rear - Zone 1 Temperature: 250-270°C, Mold Temperature: 70-95°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 40-70rpm, Shot to Cylinder Size: 40-60%, Vent Depth: 0.025-0.076mm | |