| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Elongación | 23.0 °C | 120 % Show Material materials with Elongación of 120 % | ISO 527 | 50 mm/min | ||
Elongation at yield | 23.0 °C | 6 % Show Material materials with Elongation at yield of 6 % | ISO 527 | 50 mm/min | ||
Flexural yield strength | 23.0 °C | 90 MPa Show Material materials with Flexural yield strength of 90 MPa | ISO 178 | 2 mm/min | ||
Hardness, Ball Indentation | 23.0 °C | 95 MPa Show Material materials with Hardness, Ball Indentation of 95 MPa | ISO 2039-1 | ||
Límite elástico | 23.0 °C | 63 MPa Show Material materials with Límite elástico of 63 MPa | ISO 527 | 50 mm/min | ||
Módulo de flexión | 23.0 °C | 2.3 GPa Show Material materials with Módulo de flexión of 2.3 GPa | ISO 178 | 2 mm/min | ||
Módulo elástico | 23.0 °C | 2.35 GPa Show Material materials with Módulo elástico of 2.35 GPa | ISO 527 | 1 mm/min | ||
Resistencia a la tracción | 23.0 °C | 70 MPa Show Material materials with Resistencia a la tracción of 70 MPa | ISO 527 | 50 mm/min | ||
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 35 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 35 kJ/m² | ISO 179/2C | ||
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 12 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 12 kJ/m² | ISO 180/1A | ||
23.0 °C | 70 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 70 kJ/m² | ISO 180/1A | |||
Resistencia al choque, ensayo Charpy no entallado | No Break @ 23,-30°C | ISO 179/1eU | ||||
Resistencia al choque, ensayo Izod no entallado | No Break @ 23,-30°C| ISO 180/1U | ||||
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 7E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 7E-5 1/K | ISO 11359-2 | -23°C to 80°C | ||
Conductividad térmica | 23.0 °C | 0.2 W/(m·K) Show Material materials with Conductividad térmica of 0.2 W/(m·K) | ISO 8302 | ||
Heat deflection temperature, 1.80 MPa | 127 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 127 °C | ISO 75/Ae | 1.8 MPa | |||
Relative temperature index, electrical | 130 °C Show Material materials with Relative temperature index, electrical of 130 °C | UL 746B | |||
Relative temperature index, mechanical impact | 130 °C Show Material materials with Relative temperature index, mechanical impact of 130 °C | UL 746B | |||
Relative temperature index, mechanical strength | 130 °C Show Material materials with Relative temperature index, mechanical strength of 130 °C | UL 746B | |||
Temperatura de reblandecimiento Vicat | 145 °C Show Material materials with Temperatura de reblandecimiento Vicat of 145 °C | ISO 306 | Rate B/120 | |||
Inflamabilidad | UL Recognized, 94V-0 Flame Class Rating | 6mm | UL 94 | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Constante dieléctrica | 23.0 °C | 2.7 [-] Show Material materials with Constante dieléctrica of 2.7 [-] | IEC 60250 | at 50/60 Hz |
Factor de disipación | 23.0 °C | 0.01 [-] Show Material materials with Factor de disipación of 0.01 [-] | IEC 60250 | at 1 MHz |
Rigidez dieléctrica | 23.0 °C | 17 kV/mm Show Material materials with Rigidez dieléctrica of 17 kV/mm | IEC 60243-1 | in oil, 3.2 mm |
Óptico
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.5 - 0.7 % Show Material materials with Contracción of 0.5 - 0.7 % | SABIC method |
Velocidad de flujo del volumen derretido | 6 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 6 cm³/10min | ISO 1133 | 300°C/1.2 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Building/Construction Sheet,Electronic Components,Enclosures,Heavy Vehicles,LED Lighting,Monitoring and Imaging,Non-LED Lighting,Personal Computing,Power Manangement,Travel Suitcase,Vending Machine,Water Treatment/Filtration,Window,Wireless Communications,Wiring Devices | |
| Processing methods | Drying Temperature: 120°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 290-320°C, Nozzle Temperature: 280-310°C, Front - Zone 3 Temperature: 290-320°C, Middle - Zone 2 Temperature: 280-310°C, Rear - Zone 1 Temperature: 270-300°C, Hopper Temperature: 60-80°C, Mold Temperature: 80-120°C | |