General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.16 % Show Material materials with Absorción de agua of 0.16 % | ASTM D 570 | 24 Hours |
Densidad | 23.0 °C | 1.19 g/cm³ Show Material materials with Densidad of 1.19 g/cm³ | ASTM D 792 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 110 % Show Material materials with Elongación of 110 % | ASTM D 638 | Type I, 50 mm/min |
Flexural yield strength | 23.0 °C | 81 MPa Show Material materials with Flexural yield strength of 81 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Impact strength, Izod notched, ASTM | -30.0 °C | 213 J/m Show Material materials with Impact strength, Izod notched, ASTM of 213 J/m | ASTM D 256 |
-20.0 °C | 587 J/m Show Material materials with Impact strength, Izod notched, ASTM of 587 J/m | ASTM D 256 | |
23.0 °C | 213 - 640 J/m Show Material materials with Impact strength, Izod notched, ASTM of 213 - 640 J/m | ASTM D 256 | |
Límite elástico | 23.0 °C | 57 MPa Show Material materials with Límite elástico of 57 MPa | ASTM D 638 | Type I, 50 mm/min |
Módulo de flexión | 23.0 °C | 2.03 GPa Show Material materials with Módulo de flexión of 2.03 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 6.48E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 6.48E-5 1/K | ASTM E 831 | -40°C to 95°C | ||
Heat deflection temperature, 1.80 MPa | 123 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 123 °C | ASTM D 648 | 1.82 MPa, 6.4 mm, unannealed | |||
Relative temperature index, electrical | 80 °C Show Material materials with Relative temperature index, electrical of 80 °C | UL 746B | |||
Relative temperature index, mechanical impact | 80 °C Show Material materials with Relative temperature index, mechanical impact of 80 °C | UL 746B | |||
Relative temperature index, mechanical strength | 80 °C Show Material materials with Relative temperature index, mechanical strength of 80 °C | UL 746B | |||
Inflamabilidad | UL Recognized, 94HB Flame Class Rating | 1.47mm | UL 94 | ||||
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.5 - 0.7 % Show Material materials with Contracción of 0.5 - 0.7 % | SABIC method | 3.2 mm |
Velocidad de flujo de la masa derretida | 20 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 20 g/10min | ASTM D 1238 | 300°C/1.2 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Trim | |
| Processing methods | Drying Temperature: 120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 10hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 275-300°C, Nozzle Temperature: 270-295°C, Front - Zone 3 Temperature: 275-300°C, Middle - Zone 2 Temperature: 265-290°C, Rear - Zone 1 Temperature: 255-275°C, Mold Temperature: 70-95°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 40-70rpm, Shot to Cylinder Size: 40-60%, Vent Depth: 0.025-0.076mm | |