Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.2 % Show Material materials with Absorción de agua of 0.2 % | ASTM D 570 | 50% RH, equilib |
Absorción de agua, equilibrio | 23.0 °C | 0.7 % Show Material materials with Absorción de agua, equilibrio of 0.7 % | ASTM D 570 |
Densidad | 23.0 °C | 1.22 g/cm³ Show Material materials with Densidad of 1.22 g/cm³ | ASTM D 792 |
Mecánica
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.4 [-] Show Material materials with Coeficiente de Poisson of 0.4 [-] | ASTM E 132 | ||
Elongación | 23.0 °C | 110 % Show Material materials with Elongación of 110 % | ASTM D 638 | Type I, 50 mm/min | ||
Elongation at yield | 23.0 °C | 5 % Show Material materials with Elongation at yield of 5 % | ASTM D 638 | Type I, 50 mm/min | ||
Flexural yield strength | 23.0 °C | 80 MPa Show Material materials with Flexural yield strength of 80 MPa | ISO 178 | 2 mm/min | ||
Impact strength, Izod notched, ASTM | -40.0 °C | 224 J/m Show Material materials with Impact strength, Izod notched, ASTM of 224 J/m | ASTM D 256 | ||
-30.0 °C | 245 J/m Show Material materials with Impact strength, Izod notched, ASTM of 245 J/m | ASTM D 256 | |||
-20.0 °C | 598 J/m Show Material materials with Impact strength, Izod notched, ASTM of 598 J/m | ASTM D 256 | |||
23.0 °C | 699 J/m Show Material materials with Impact strength, Izod notched, ASTM of 699 J/m | ASTM D 256 | |||
Límite elástico | 23.0 °C | 49 MPa Show Material materials with Límite elástico of 49 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Módulo de flexión | 23.0 °C | 2.2 GPa Show Material materials with Módulo de flexión of 2.2 GPa | ISO 178 | 2 mm/min | ||
Módulo elástico | 23.0 °C | 2.09 GPa Show Material materials with Módulo elástico of 2.09 GPa | ASTM D 638 | 50 mm/min | ||
Resistencia a la tracción | 23.0 °C | 49 MPa Show Material materials with Resistencia a la tracción of 49 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Resistencia al choque, ensayo Charpy entallado | -30.0 °C | 35 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 35 kJ/m² | ISO 179/1eA | ||
23.0 °C | 45 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 45 kJ/m² | ISO 179/1eA | |||
Resistencia al choque, ensayo Izod entallado | -40.0 °C | 15 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 15 kJ/m² | ISO 180/1A | ||
-30.0 °C | 25 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 25 kJ/m² | ISO 180/1A | |||
-20.0 °C | 35 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 35 kJ/m² | ISO 180/1A | |||
-10.0 °C | 38 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 38 kJ/m² | ISO 180/1A | |||
23.0 °C | 40 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 40 kJ/m² | ISO 180/1A | |||
Resistencia al choque, ensayo Charpy no entallado | No break @ 23,-30°C | ISO 179/1eU | ||||
Resistencia al choque, ensayo Izod no entallado | No break @ 23,-30°C | ISO 180/1U | ||||
Aplicaciones térmicas
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 7.56E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 7.56E-5 1/K | ASTM D 696 | -30°C to 30°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 7.92E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 7.92E-5 1/K | ASTM D 696 | -30°C to 30°C |
Conductividad térmica | 23.0 °C | 0.18 W/(m·K) Show Material materials with Conductividad térmica of 0.18 W/(m·K) | ASTM C177 |
Heat deflection temperature, 1.80 MPa | 105 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 105 °C | ISO 75/Ae | 1.8 MPa | |
Temperatura de reblandecimiento Vicat | 135 °C Show Material materials with Temperatura de reblandecimiento Vicat of 135 °C | ISO 306 | Rate B/120 |
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Constante dieléctrica | 23.0 °C | 3.1 [-] Show Material materials with Constante dieléctrica of 3.1 [-] | ASTM D 150 | at 1 MHz |
Factor de disipación | 23.0 °C | 0.02 [-] Show Material materials with Factor de disipación of 0.02 [-] | ASTM D 150 | at 1 MHz |
Rigidez dieléctrica | 23.0 °C | 16.9 kV/mm Show Material materials with Rigidez dieléctrica of 16.9 kV/mm | ASTM D 149 | in oil, 3.2 mm |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.5 - 0.8 % Show Material materials with Contracción of 0.5 - 0.8 % | SABIC method |
Contracción transversal | 23.0 °C | 0.5 - 0.8 % Show Material materials with Contracción transversal of 0.5 - 0.8 % | SABIC method |
Velocidad de flujo del volumen derretido | 4 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 4 cm³/10min | ISO 1133 | 265°C/1.2 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Door Handle,Wiring Devices | |
| Processing methods | Drying Temperature: 110°C, Drying Time: 4-6hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 260-275°C, Nozzle Temperature: 255-270°C, Front - Zone 3 Temperature: 255-275°C, Middle - Zone 2 Temperature: 250-270°C, Rear - Zone 1 Temperature: 245-265°C, Mold Temperature: 65-90°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 50-80rpm, Shot to Cylinder Size: 50-80%, Vent Depth: 0.013-0.02mm | |