General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.37 g/cm³ Show Material materials with Densidad of 1.37 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.41 [-] Show Material materials with Coeficiente de Poisson of 0.41 [-] | |||
Dureza Rockwell M | 23.0 °C | 64.6 [-] Show Material materials with Dureza Rockwell M of 64.6 [-] | ISO 2039-2 | ||
Elongación | 23.0 °C | 500 % Show Material materials with Elongación of 500 % | min. | ISO 527-1/-2 | ||
Elongation at yield | 23.0 °C | 25 % Show Material materials with Elongation at yield of 25 % | ISO 527-1/-2 | ||
Hardness, Rockwell R | 23.0 °C | 113 [-] Show Material materials with Hardness, Rockwell R of 113 [-] | ISO 2039-2 | ||
Límite elástico | 23.0 °C | 54 MPa Show Material materials with Límite elástico of 54 MPa | ISO 527-1/-2 | ||
Módulo de flexión | 23.0 °C | 1.85 GPa Show Material materials with Módulo de flexión of 1.85 GPa | ISO 178 | ||
Módulo elástico | 23.0 °C | 1.9 GPa Show Material materials with Módulo elástico of 1.9 GPa | ISO 527-1/-2 | ||
Resistencia al choque, ensayo Charpy entallado | -6.0 °C | 14 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 14 kJ/m² | ISO 179/1eA | ||
23.0 °C | 25 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 25 kJ/m² | ISO 179/1eA | |||
Resistencia al choque, ensayo Charpy no entallado | No Break @ 23,-6°C, ISO 179/1eA |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 1.2E-4 1/K Show Material materials with Coeficiente de dilatación térmica of 1.2E-4 1/K | ISO 11359-1/-2 | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.2E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1.2E-4 1/K | ISO 11359-1/-2 | ||
Heat deflection temperature, 0.45 MPa | 126 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 126 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 71 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 71 °C | ISO 75-1/-2 | |||
Temperatura de fusión | 178 °C Show Material materials with Temperatura de fusión of 178 °C | ISO 11357-1/-3 | 18°F/min | |||
Temperatura de reblandecimiento Vicat | 173 °C Show Material materials with Temperatura de reblandecimiento Vicat of 173 °C | ISO 306 | 90°F, 2 lbf | |||
Inflamabilidad | FMVSS Class: B -, Burning rate, Thickness 1 mm: 42 mm/min |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 1.3 % Show Material materials with Contracción of 1.3 % | ISO 294-4, 2577 |
Contracción transversal | 23.0 °C | 1.5 % Show Material materials with Contracción transversal of 1.5 % | ISO 294-4, 2577 |
Velocidad de flujo de la masa derretida | 2.2 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 2.2 g/10min | ISO 1133 | 190°C/2.16kg | |
Velocidad de flujo del volumen derretido | 2 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 2 cm³/10min | ISO 1133 |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 4-8h, Processing Moisture Content: ≤0.05%, Melt Temperature Optimum: 205°C, Min. melt temperature: 200°C, Max. melt temperature: 210°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 50°C, Min. mold temperature: 40°C, Max. mold temperature: 60°C, Hold pressure range: 60-80MPa, Hold pressure time: 7.5s/mm |