| Property | Temperature | Value | Comment |
|---|---|---|---|
Densidad | 23.0 °C | 1.33 g/cm³ Show Material materials with Densidad of 1.33 g/cm³ | ISO 1183 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.43 [-] Show Material materials with Coeficiente de Poisson of 0.43 [-] | |
Elongación | 23.0 °C | 500 % Show Material materials with Elongación of 500 % | min. | ISO 527-1/-2 |
Elongation at yield | 23.0 °C | 30 % Show Material materials with Elongation at yield of 30 % | ISO 527-1/-2 |
Límite elástico | 23.0 °C | 40 MPa Show Material materials with Límite elástico of 40 MPa | ISO 527-1/-2 |
Módulo de flexión | 23.0 °C | 1.1 GPa Show Material materials with Módulo de flexión of 1.1 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 1.4 GPa Show Material materials with Módulo elástico of 1.4 GPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -6.0 °C | 14 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 14 kJ/m² | ISO 179/1eA |
23.0 °C | 80 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 80 kJ/m² | ISO 179/1eA | |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 1.2E-4 1/K Show Material materials with Coeficiente de dilatación térmica of 1.2E-4 1/K | ISO 11359-1/-2 | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.2E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1.2E-4 1/K | ISO 11359-1/-2 | ||
Heat deflection temperature, 0.45 MPa | 102 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 102 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 60 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 60 °C | ISO 75-1/-2 | |||
Relative temperature index, electrical | 105 °C Show Material materials with Relative temperature index, electrical of 105 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 85 °C Show Material materials with Relative temperature index, mechanical impact of 85 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 85 °C Show Material materials with Relative temperature index, mechanical strength of 85 °C | UL 746B | 120mil | |||
Temperatura de fusión | 178 °C Show Material materials with Temperatura de fusión of 178 °C | ISO 11357-1/-3 | 18°F/min | |||
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min | ||||
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.8 % Show Material materials with Contracción of 0.8 % | ISO 294-4, 2577 |
Contracción transversal | 23.0 °C | 1.1 % Show Material materials with Contracción transversal of 1.1 % | ISO 294-4, 2577 |
Velocidad de flujo de la masa derretida | 2.1 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 2.1 g/10min | ISO 1133 | 190°C/2.16kg | |
Velocidad de flujo del volumen derretido | 1.8 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 1.8 cm³/10min | ISO 1133 |
Technological properties
| Property | ||
|---|---|---|
| Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 4-8h, Processing Moisture Content: ≤0.05%, Melt Temperature Optimum: 205°C, Min. melt temperature: 200°C, Max. melt temperature: 210°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 50°C, Min. mold temperature: 40°C, Max. mold temperature: 60°C, Hold pressure range: 60-80MPa, Hold pressure time: 7.5s/mm | |