General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Densidad | 23.0 °C | 1.42 g/cm³ Show Material materials with Densidad of 1.42 g/cm³ | ISO 1183 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.37 [-] Show Material materials with Coeficiente de Poisson of 0.37 [-] | |
Elongación | 23.0 °C | 37 % Show Material materials with Elongación of 37 % | ISO 527-1/-2 |
Elongation at yield | 23.0 °C | 22 % Show Material materials with Elongation at yield of 22 % | ISO 527-1/-2 |
Límite elástico | 23.0 °C | 71.5 MPa Show Material materials with Límite elástico of 71.5 MPa | ISO 527-1/-2 |
Módulo de flexión | 23.0 °C | 2.8 GPa Show Material materials with Módulo de flexión of 2.8 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 3 GPa Show Material materials with Módulo elástico of 3 GPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -6.0 °C | 10 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 10 kJ/m² | ISO 179/1eA |
23.0 °C | 13 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 13 kJ/m² | ISO 179/1eA | |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 1.1E-4 1/K Show Material materials with Coeficiente de dilatación térmica of 1.1E-4 1/K | ISO 11359-1/-2 | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.1E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1.1E-4 1/K | ISO 11359-1/-2 | ||
Heat deflection temperature, 0.45 MPa | 162 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 162 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 92 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 92 °C | ISO 75-1/-2 | |||
Relative temperature index, electrical | 50 °C Show Material materials with Relative temperature index, electrical of 50 °C | UL 746B | 30mil | |||
Relative temperature index, mechanical impact | 50 °C Show Material materials with Relative temperature index, mechanical impact of 50 °C | UL 746B | 30mil | |||
Relative temperature index, mechanical strength | 50 °C Show Material materials with Relative temperature index, mechanical strength of 50 °C | UL 746B | 30mil | |||
Temperatura de fusión | 178 °C Show Material materials with Temperatura de fusión of 178 °C | ISO 11357-1/-3 | 18°F/min | |||
Inflamabilidad | Burning Behav. at thickness h: HB class, Thickness tested: 0.8 mm, UL recognition: yes -, FMVSS Class: B -, Burning rate, Thickness 1 mm: 26 mm/min | ||||
Rheological Properties
| Property | Value | Comment |
|---|---|---|
Velocidad de flujo de la masa derretida | 2.5 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 2.5 g/10min | ISO 1133 | 190°C/2.16kg |
Technological properties
| Property | ||
|---|---|---|
| Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 215°C, Min. melt temperature: 210°C, Max. melt temperature: 220°C, Mold Temperature Optimum: 90°C, Min. mold temperature: 80°C, Max. mold temperature: 100°C, Hold pressure range: 90-110MPa, Hold pressure time: 8s/mm | |