General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.37 g/cm³ Show Material materials with Densidad of 1.37 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.34 [-] Show Material materials with Coeficiente de Poisson of 0.34 [-] | |
Elongación | 23.0 °C | 3 % Show Material materials with Elongación of 3 % | ISO 527-1/-2 |
Módulo de flexión | 23.0 °C | 9 GPa Show Material materials with Módulo de flexión of 9 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 10 GPa Show Material materials with Módulo elástico of 10 GPa | ISO 527-1/-2 |
Resistencia a la flexión | 23.0 °C | 280 MPa Show Material materials with Resistencia a la flexión of 280 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 190 MPa Show Material materials with Resistencia a la tracción of 190 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -6.0 °C | 8 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 8 kJ/m² | ISO 179/1eA |
23.0 °C | 10 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 10 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Charpy no entallado | 23.0 °C | 65 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 65 kJ/m² | ISO 179/1eU |
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 10 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 10 kJ/m² | ISO 180/1A |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Calor específico | 23.0 °C | 2220 J/(kg·K) Show Material materials with Calor específico of 2220 J/(kg·K) | of melt | ||
Heat deflection temperature, 1.80 MPa | 253 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 253 °C | ISO 75-1/-2 | |||
Relative temperature index, electrical | 140 °C Show Material materials with Relative temperature index, electrical of 140 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 125 °C Show Material materials with Relative temperature index, mechanical impact of 125 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 140 °C Show Material materials with Relative temperature index, mechanical strength of 140 °C | UL 746B | 120mil | |||
Temperatura de fusión | 262 °C Show Material materials with Temperatura de fusión of 262 °C | ISO 11357-1/-3 | 18°F/min | |||
Temperatura de transición del vidrio | 75 °C Show Material materials with Temperatura de transición del vidrio of 75 °C | ISO 11357-1/-2 | 18°F/min | |||
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.75 mm, UL recognition: yes -, Oxygen index: 24 %, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min, Hot Wire Ignition, 30mil: 7 s, Hot Wire Ignition, 60mil: 7 s, Hot Wire Ignition, 120mil: 60 s |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Índice de seguimiento comparativo | 23.0 °C | 400 V Show Material materials with Índice de seguimiento comparativo of 400 V | IEC 60112 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 30% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 295°C, Min. melt temperature: 285°C, Max. melt temperature: 305°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm |