General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 0.8 % Show Material materials with Absorción de agua of 0.8 % | Sim. to ISO 62 | Immersion 24h |
Densidad | 23.0 °C | 1.58 g/cm³ Show Material materials with Densidad of 1.58 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | |
Elongación | 23.0 °C | 2.6 % Show Material materials with Elongación of 2.6 % | ISO 527-1/-2 |
Hardness, Ball Indentation | 23.0 °C | 300 MPa Show Material materials with Hardness, Ball Indentation of 300 MPa | ISO 2039-1 |
Módulo de flexión | 23.0 °C | 16 GPa Show Material materials with Módulo de flexión of 16 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 17 GPa Show Material materials with Módulo elástico of 17 GPa | ISO 527-1/-2 |
Resistencia a la flexión | 23.0 °C | 390 MPa Show Material materials with Resistencia a la flexión of 390 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 240 MPa Show Material materials with Resistencia a la tracción of 240 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -6.0 °C | 14 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 14 kJ/m² | ISO 179/1eA |
23.0 °C | 17 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 17 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Charpy no entallado | -6.0 °C | 100 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 100 kJ/m² | ISO 179/1eU |
23.0 °C | 100 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 100 kJ/m² | ISO 179/1eU | |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 1.7E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.7E-5 1/K | ASTM E 831 | 55 - 160°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 6.1E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 6.1E-5 1/K | ASTM E 831 | 23 - 55°C | ||
Heat deflection temperature, 1.80 MPa | 258 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 258 °C | ISO 75-1/-2 | |||
Relative temperature index, electrical | 120 °C Show Material materials with Relative temperature index, electrical of 120 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 130 °C Show Material materials with Relative temperature index, mechanical impact of 130 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 130 °C Show Material materials with Relative temperature index, mechanical strength of 130 °C | UL 746B | 120mil | |||
Temperatura de fusión | 262 °C Show Material materials with Temperatura de fusión of 262 °C | ISO 11357-1/-3 | 18°F/min | |||
Temperatura de reblandecimiento Vicat | 255 °C Show Material materials with Temperatura de reblandecimiento Vicat of 255 °C | ISO 306 | 90°F/h, 11 lbf | |||
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.83 mm, UL recognition: yes -, Glow Wire Flammability Index, 30mil: 650 °C, Glow Wire Flammability Index, 60mil: 675 °C, Glow Wire Flammability Index, 120mil: 850 °C, Glow Wire Ignition Temperature, 30mil: 700 °C, FMVSS Class: SE - |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 50% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 295°C, Min. melt temperature: 285°C, Max. melt temperature: 305°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C |