General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 6.8 % Show Material materials with Absorción de agua of 6.8 % | Sim. to ISO 62 | 80mil |
Coefficient of friction | 0.55 [-] Show Material materials with Coefficient of friction of 0.55 [-] | ASTM 1894 | 1h against steel | |
Densidad | 23.0 °C | 1.19 g/cm³ Show Material materials with Densidad of 1.19 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.35 [-] Show Material materials with Coeficiente de Poisson of 0.35 [-] | |
Elongación | 23.0 °C | 5.2 % Show Material materials with Elongación of 5.2 % | ISO 527-1/-2 |
Módulo de flexión | 23.0 °C | 4.9 GPa Show Material materials with Módulo de flexión of 4.9 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 5.3 GPa Show Material materials with Módulo elástico of 5.3 GPa | ISO 527-1/-2 |
Resistencia a la tracción | 23.0 °C | 110 MPa Show Material materials with Resistencia a la tracción of 110 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -6.0 °C | 5 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 5 kJ/m² | ISO 179/1eA |
23.0 °C | 6 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 6 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Charpy no entallado | -6.0 °C | 40 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 40 kJ/m² | ISO 179/1eU |
23.0 °C | 50 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 50 kJ/m² | ISO 179/1eU | |
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 5 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 5 kJ/m² | ISO 180/1A |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 4.7E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 4.7E-5 1/K | ISO 11359-1/-2 | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 7.5E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 7.5E-5 1/K | ISO 11359-1/-2 | ||
Heat deflection temperature, 0.45 MPa | 255 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 255 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 222 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 222 °C | ISO 75-1/-2 | |||
Temperatura de fusión | 263 °C Show Material materials with Temperatura de fusión of 263 °C | ISO 11357-1/-3 | 18°F/min | |||
Temperatura de reblandecimiento Vicat | 240 °C Show Material materials with Temperatura de reblandecimiento Vicat of 240 °C | ISO 306 | 90°F/h, 11 lbf | |||
Temperatura de transición del vidrio | 80 °C Show Material materials with Temperatura de transición del vidrio of 80 °C | ISO 11357-1/-2 | 18°F/min | |||
Inflamabilidad | FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Dissipation factor, 100Hz | 23.0 °C | 0.01 [-] Show Material materials with Dissipation factor, 100Hz of 0.01 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.01 [-] Show Material materials with Dissipation factor, 1MHz of 0.01 [-] | IEC 62631-2-1 |
Rigidez dieléctrica | 23.0 °C | 23 kV/mm Show Material materials with Rigidez dieléctrica of 23 kV/mm | IEC 60243-1 |
Volume resistivity | 23.0 °C | 1.00E+11 Ω·cm Show Material materials with Volume resistivity of 1.00E+11 Ω·cm | IEC 62631-3-1 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 20% Aramid Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 290°C, Min. melt temperature: 285°C, Max. melt temperature: 305°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 110°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C |