General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.75 % Show Material materials with Absorción de agua of 0.75 % | Sim. to ISO 62 | 80mil |
Densidad | 23.0 °C | 1.64 g/cm³ Show Material materials with Densidad of 1.64 g/cm³ | ISO 1183 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | |
Elongación | 23.0 °C | 2 % Show Material materials with Elongación of 2 % | ISO 527-1/-2 |
Hardness, Rockwell R | 23.0 °C | 115 [-] Show Material materials with Hardness, Rockwell R of 115 [-] | ISO 2039-2 |
Módulo de flexión | 23.0 °C | 12 GPa Show Material materials with Módulo de flexión of 12 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 12 GPa Show Material materials with Módulo elástico of 12 GPa | ISO 527-1/-2 |
Resistencia a la compresión | 23.0 °C | 180 MPa Show Material materials with Resistencia a la compresión of 180 MPa | ISO 604 |
Resistencia a la flexión | 23.0 °C | 200 MPa Show Material materials with Resistencia a la flexión of 200 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 110 MPa Show Material materials with Resistencia a la tracción of 110 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 7 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 7 kJ/m² | ISO 179/1eA |
Resistencia al choque, ensayo Charpy no entallado | 23.0 °C | 30 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 30 kJ/m² | ISO 179/1eU |
Resistencia al cizallamiento | 23.0 °C | 60 MPa Show Material materials with Resistencia al cizallamiento of 60 MPa | ASTM D 732 |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 2.5E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 2.5E-5 1/K | ISO 11359-1/-2 | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 6E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 6E-5 1/K | ISO 11359-1/-2 | ||
Heat deflection temperature, 0.45 MPa | 240 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 240 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 220 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 220 °C | ISO 75-1/-2 | |||
Temperatura de fusión | 250 °C Show Material materials with Temperatura de fusión of 250 °C | ISO 11357-1/-3 | 18°F/min | |||
Inflamabilidad | Glow Wire Flammability Index, 40mil: 750 °C, Glow Wire Flammability Index, 80mil: 775 °C, Glow Wire Flammability Index, 120mil: 960 °C, Glow Wire Ignition Temperature, 40mil: 750 °C, Glow Wire Ignition Temperature, 80mil: 775 °C, Glow Wire Ignition Temperature, 120mil: 875 °C, Glow Wire Temperature, No Flame, 40mil: 750 °C, Glow Wire Temperature, No Flame, 80mil: 775 °C, Glow Wire Temperature, No Flame, 120mil: 850 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: 22 mm/min | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Constante dieléctrica, 1 MHz | 23.0 °C | 3.7 [-] Show Material materials with Constante dieléctrica, 1 MHz of 3.7 [-] | IEC 62631-2-1 |
Constante dieléctrica, 100 Hz | 23.0 °C | 3.8 [-] Show Material materials with Constante dieléctrica, 100 Hz of 3.8 [-] | IEC 62631-2-1 |
Dissipation factor, 100Hz | 23.0 °C | 7E-3 [-] Show Material materials with Dissipation factor, 100Hz of 7E-3 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 1MHz of 0.02 [-] | IEC 62631-2-1 |
Rigidez dieléctrica | 23.0 °C | 38 kV/mm Show Material materials with Rigidez dieléctrica of 38 kV/mm | IEC 60243-1 |
Surface resistivity | 23.0 °C | 1.00E+14 Ω/sq Show Material materials with Surface resistivity of 1.00E+14 Ω/sq | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | IEC 62631-3-1 |
Rheological Properties
Technological properties
| Property | ||
|---|---|---|
| Fillers | 40% Glass Fiber and Mineral Powder | |
| Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 4-6h, Processing Moisture Content: ≤0.02%, Melt Temperature Optimum: 285°C, Min. melt temperature: 280°C, Max. melt temperature: 300°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 110°C, Min. mold temperature: 100°C, Max. mold temperature: 120°C, Hold pressure range: ≥80MPa, Hold pressure time: 4s/mm, Back pressure: As low as possible, Ejection temperature: 170°C | |