General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 4.9 % Show Material materials with Absorción de agua of 4.9 % | Sim. to ISO 62 | 80mil |
Densidad | 23.0 °C | 1.51 g/cm³ Show Material materials with Densidad of 1.51 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | |
Elongación | 23.0 °C | 3 % Show Material materials with Elongación of 3 % | ISO 527-1/-2 |
Módulo elástico | 23.0 °C | 14.2 GPa Show Material materials with Módulo elástico of 14.2 GPa | ISO 527-1/-2 |
Resistencia a la tracción | 23.0 °C | 215 MPa Show Material materials with Resistencia a la tracción of 215 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 19 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 19 kJ/m² | ISO 179/1eA |
Resistencia al choque, ensayo Charpy no entallado | 23.0 °C | 100 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 100 kJ/m² | ISO 179/1eU |
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 17 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 17 kJ/m² | ISO 180/1A |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Calor específico | 23.0 °C | 2100 J/(kg·K) Show Material materials with Calor específico of 2100 J/(kg·K) | of melt | ||
Heat deflection temperature, 1.80 MPa | 218 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 218 °C | ISO 75-1/-2 | |||
Temperatura de fusión | 221 °C Show Material materials with Temperatura de fusión of 221 °C | ISO 11357-1/-3 | 18°F/min | |||
Inflamabilidad | FMVSS Class: B -, Burning rate, Thickness 1 mm: 44 mm/min |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Índice de seguimiento comparativo | 23.0 °C | 500 V Show Material materials with Índice de seguimiento comparativo of 500 V | IEC 60112 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 45% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 270°C, Min. melt temperature: 260°C, Max. melt temperature: 280°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C |