Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 6.3 % Show Material materials with Absorción de agua of 6.3 % | Sim. to ISO 62 | 80mil |
Densidad | 23.0 °C | 1.36 g/cm³ Show Material materials with Densidad of 1.36 g/cm³ | ISO 1183 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.34 [-] Show Material materials with Coeficiente de Poisson of 0.34 [-] | |
Elongación | 23.0 °C | 3.5 % Show Material materials with Elongación of 3.5 % | ISO 527-1/-2 |
Hardness, Ball Indentation | 23.0 °C | 233 MPa Show Material materials with Hardness, Ball Indentation of 233 MPa | ISO 2039-1 |
Módulo de flexión | 23.0 °C | 8.5 GPa Show Material materials with Módulo de flexión of 8.5 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 10 GPa Show Material materials with Módulo elástico of 10 GPa | ISO 527-1/-2 |
Resistencia a la compresión | 23.0 °C | 160 MPa Show Material materials with Resistencia a la compresión of 160 MPa | ISO 604 |
Resistencia a la flexión | 23.0 °C | 240 MPa Show Material materials with Resistencia a la flexión of 240 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 180 MPa Show Material materials with Resistencia a la tracción of 180 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -40.0 °C | 11 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 11 kJ/m² | ISO 179/1eA |
-6.0 °C | 11 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 11 kJ/m² | ISO 179/1eA | |
23.0 °C | 14 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 14 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Charpy no entallado | -6.0 °C | 80 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 80 kJ/m² | ISO 179/1eU |
23.0 °C | 90 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 90 kJ/m² | ISO 179/1eU | |
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 90 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 90 kJ/m² | ISO 180/1U |
23.0 °C | 100 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 100 kJ/m² | ISO 180/1U | |
Resistencia al choque, ensayo Izod no entallado | -40.0 °C | 11 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 11 kJ/m² | ISO 180/1A |
-30.0 °C | 11 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 11 kJ/m² | ISO 180/1A | |
23.0 °C | 15 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 15 kJ/m² | ISO 180/1A | |
Resistencia al cizallamiento | 23.0 °C | 60 MPa Show Material materials with Resistencia al cizallamiento of 60 MPa | ASTM D 732 |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 1.4E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.4E-5 1/K | ISO 11359-1/-2 | 23 - 55°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.3E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1.3E-4 1/K | ISO 11359-1/-2 | 55 - 160°C | ||
Heat deflection temperature, 0.45 MPa | 220 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 220 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 210 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 210 °C | ISO 75-1/-2 | |||
Relative temperature index, electrical | 65 °C Show Material materials with Relative temperature index, electrical of 65 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 65 °C Show Material materials with Relative temperature index, mechanical impact of 65 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 65 °C Show Material materials with Relative temperature index, mechanical strength of 65 °C | UL 746B | 120mil | |||
Temperatura de fusión | 221 °C Show Material materials with Temperatura de fusión of 221 °C | ISO 11357-1/-3 | 18°F/min | |||
Temperatura de transición del vidrio | 60 °C Show Material materials with Temperatura de transición del vidrio of 60 °C | ISO 11357-1/-2 | 18°F/min | |||
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 3 mm, UL recognition: yes -, Oxygen index: 21 %, Glow Wire Flammability Index, 40mil: 700 °C, Glow Wire Flammability Index, 80mil: 700 °C, Glow Wire Flammability Index, 120mil: 750 °C, Glow Wire Ignition Temperature, 40mil: 700 °C, Glow Wire Ignition Temperature, 80mil: 700 °C, Glow Wire Ignition Temperature, 120mil: 700 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: 25 mm/min | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Constante dieléctrica, 100 Hz | 23.0 °C | 3.8 [-] Show Material materials with Constante dieléctrica, 100 Hz of 3.8 [-] | IEC 62631-2-1 |
Dissipation factor, 100Hz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 100Hz of 0.02 [-] | IEC 62631-2-1 |
Volume resistivity | 23.0 °C | 1.00E+14 Ω·cm Show Material materials with Volume resistivity of 1.00E+14 Ω·cm | IEC 62631-3-1 |
Índice de seguimiento comparativo | 23.0 °C | 0 V Show Material materials with Índice de seguimiento comparativo of 0 V | UL 746A |
Rheological Properties
Technological properties
| Property | ||
|---|---|---|
| Fillers | 30% Glass Fiber | |
| Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 270°C, Min. melt temperature: 260°C, Max. melt temperature: 280°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm | |