General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 0.1 % Show Material materials with Absorción de agua of 0.1 % | Sim. to ISO 62 | Immersion 24h |
Densidad | 23.0 °C | 1.42 g/cm³ Show Material materials with Densidad of 1.42 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | |
Elongación | 23.0 °C | 3 % Show Material materials with Elongación of 3 % | ISO 527-1/-2 |
Hardness, Rockwell R | 23.0 °C | 118 [-] Show Material materials with Hardness, Rockwell R of 118 [-] | ISO 2039-2 |
Módulo de flexión | 23.0 °C | 11 GPa Show Material materials with Módulo de flexión of 11 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 12.5 GPa Show Material materials with Módulo elástico of 12.5 GPa | ISO 527-1/-2 |
Resistencia a la tracción | 23.0 °C | 200 MPa Show Material materials with Resistencia a la tracción of 200 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -40.0 °C | 17 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 17 kJ/m² | ISO 179/1eA |
-6.0 °C | 17 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 17 kJ/m² | ISO 179/1eA | |
23.0 °C | 17 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 17 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Charpy no entallado | -6.0 °C | 85 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 85 kJ/m² | ISO 179/1eU |
23.0 °C | 100 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 100 kJ/m² | ISO 179/1eU | |
Resistencia al choque, ensayo Izod no entallado | -40.0 °C | 15 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 15 kJ/m² | ISO 180/1A |
23.0 °C | 17 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 17 kJ/m² | ISO 180/1A | |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 1.3E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.3E-5 1/K | ISO 11359-1/-2 | 23 - 55°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.4E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1.4E-4 1/K | ISO 11359-1/-2 | 55 - 160°C | ||
Heat deflection temperature, 0.45 MPa | 217 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 217 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 203 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 203 °C | ISO 75-1/-2 | |||
Relative temperature index, electrical | 120 °C Show Material materials with Relative temperature index, electrical of 120 °C | UL 746B | 60mil | |||
Relative temperature index, mechanical strength | 120 °C Show Material materials with Relative temperature index, mechanical strength of 120 °C | UL 746B | 60mil | |||
Temperatura de fusión | 218 °C Show Material materials with Temperatura de fusión of 218 °C | ISO 11357-1/-3 | 18°F/min | |||
Temperatura de transición del vidrio | 65 °C Show Material materials with Temperatura de transición del vidrio of 65 °C | ISO 11357-1/-2 | 18°F/min | |||
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.71 mm, UL recognition: yes -, Glow Wire Flammability Index, 40mil: 750 °C, Glow Wire Flammability Index, 80mil: 750 °C, Glow Wire Flammability Index, 120mil: 775 °C, Glow Wire Ignition Temperature, 40mil: 750 °C, Glow Wire Ignition Temperature, 80mil: 750 °C, Glow Wire Ignition Temperature, 120mil: 775 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: 21 mm/min |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Constante dieléctrica, 1 MHz | 23.0 °C | 3.6 [-] Show Material materials with Constante dieléctrica, 1 MHz of 3.6 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 1MHz of 0.02 [-] | IEC 62631-2-1 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | IEC 62631-3-1 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 43% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 290°C, Min. melt temperature: 280°C, Max. melt temperature: 300°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C |