Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.83 % Show Material materials with Absorción de agua of 0.83 % | Sim. to ISO 62 | Immersion 24h |
Densidad | 23.0 °C | 1.32 g/cm³ Show Material materials with Densidad of 1.32 g/cm³ | ISO 1183 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.34 [-] Show Material materials with Coeficiente de Poisson of 0.34 [-] | |
Elongación | 23.0 °C | 4 % Show Material materials with Elongación of 4 % | ISO 527-1/-2 |
Hardness, Ball Indentation | 23.0 °C | 220 MPa Show Material materials with Hardness, Ball Indentation of 220 MPa | ISO 2039-1 |
Módulo de flexión | 23.0 °C | 7.4 GPa Show Material materials with Módulo de flexión of 7.4 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 8.7 GPa Show Material materials with Módulo elástico of 8.7 GPa | ISO 527-1/-2 |
Resistencia a la flexión | 23.0 °C | 205 MPa Show Material materials with Resistencia a la flexión of 205 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 142 MPa Show Material materials with Resistencia a la tracción of 142 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -40.0 °C | 13 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 13 kJ/m² | ISO 179/1eA |
-6.0 °C | 14 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 14 kJ/m² | ISO 179/1eA | |
23.0 °C | 20 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 20 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Charpy no entallado | -6.0 °C | 80 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 80 kJ/m² | ISO 179/1eU |
23.0 °C | 91 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 91 kJ/m² | ISO 179/1eU | |
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 80 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 80 kJ/m² | ISO 180/1U |
23.0 °C | 74 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 74 kJ/m² | ISO 180/1U | |
Resistencia al choque, ensayo Izod no entallado | -40.0 °C | 15 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 15 kJ/m² | ISO 180/1A |
-30.0 °C | 14 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 14 kJ/m² | ISO 180/1A | |
23.0 °C | 21 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 21 kJ/m² | ISO 180/1A | |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Calor específico | 23.0 °C | 2200 J/(kg·K) Show Material materials with Calor específico of 2200 J/(kg·K) | of melt | ||
Coeficiente de dilatación térmica | 23.0 °C | 1.5E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.5E-5 1/K | ISO 11359-1/-2 | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.2E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1.2E-4 1/K | ISO 11359-1/-2 | ||
Difusividad térmica | 23.0 °C | 0 mm²/s Show Material materials with Difusividad térmica of 0 mm²/s | |||
Heat deflection temperature, 0.45 MPa | 262 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 262 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 247 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 247 °C | ISO 75-1/-2 | |||
Relative temperature index, electrical | 120 °C Show Material materials with Relative temperature index, electrical of 120 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 105 °C Show Material materials with Relative temperature index, mechanical impact of 105 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 105 °C Show Material materials with Relative temperature index, mechanical strength of 105 °C | UL 746B | 120mil | |||
Temperatura de fusión | 262 °C Show Material materials with Temperatura de fusión of 262 °C | ISO 11357-1/-3 | 18°F/min | |||
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.75 mm, UL recognition: yes -, Oxygen index: 23 %, Glow Wire Flammability Index, 30mil: 650 °C, Glow Wire Flammability Index, 40mil: 650 °C, Glow Wire Flammability Index, 60mil: 650 °C, Glow Wire Flammability Index, 120mil: 775 °C, Glow Wire Ignition Temperature, 30mil: 675 °C, Glow Wire Ignition Temperature, 60mil: 675 °C, Glow Wire Ignition Temperature, 120mil: 725 °C, FMVSS Class: SE -, Burning rate, Thickness 1 mm: 23 mm/min | ||||
Rheological Properties
Technological properties
| Property | ||
|---|---|---|
| Fillers | 33% Glass Fiber | |
| Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 295°C, Min. melt temperature: 285°C, Max. melt temperature: 305°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 80°C, Min. mold temperature: 50°C, Max. mold temperature: 100°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C | |