General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.01 g/cm³ Show Material materials with Densidad of 1.01 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.45 [-] Show Material materials with Coeficiente de Poisson of 0.45 [-] | |
Dureza Shore D | 23.0 °C | 69 [-] Show Material materials with Dureza Shore D of 69 [-] | ISO 7619-1 | 15 seconds |
Elongación | 23.0 °C | 100 % Show Material materials with Elongación of 100 % | ISO 527-1/-2 | 50mm/min |
Elongation at yield | 23.0 °C | 12 % Show Material materials with Elongation at yield of 12 % | ISO 527-1/-2 |
Límite elástico | 23.0 °C | 32 MPa Show Material materials with Límite elástico of 32 MPa | ISO 527-1/-2 |
Módulo elástico | 23.0 °C | 1.1 GPa Show Material materials with Módulo elástico of 1.1 GPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -6.0 °C | 13 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 13 kJ/m² | ISO 179/1eA |
23.0 °C | 35 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 35 kJ/m² | ISO 179/1eA | |
Aplicaciones térmicas
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 0.45 MPa | 83 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 83 °C | ISO 75-1/-2 | |
Heat deflection temperature, 1.80 MPa | 47 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 47 °C | ISO 75-1/-2 | |
Temperatura de fusión | 216 °C Show Material materials with Temperatura de fusión of 216 °C | ISO 11357-1/-3 | 18°F/min | |
Inflamabilidad | FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Technological properties
Property |
---|