Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of friction | 0.25 [-] Show Material materials with Coefficient of friction of 0.25 [-] | ASTM D1894, polymer to steel, static value, dynamic value: 0.16 | |
Densidad | 23.0 °C | 1.13 g/cm³ Show Material materials with Densidad of 1.13 g/cm³ | ASTM D792 |
Mecánica
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Elongación | 23.0 °C | 3 % Show Material materials with Elongación of 3 % | ASTM D638 | ||
121.0 °C | 7 % Show Material materials with Elongación of 7 % | ASTM D638 | |||
Elongation at yield | 23.0 °C | 3 % Show Material materials with Elongation at yield of 3 % | ASTM D638 | ||
121.0 °C | 7 % Show Material materials with Elongation at yield of 7 % | ASTM D638 | |||
Hardness, Rockwell R | 23.0 °C | 121 [-] Show Material materials with Hardness, Rockwell R of 121 [-] | ASTM D785 | ||
Impact strength, Izod notched, ASTM | 23.0 °C | 117 J/m Show Material materials with Impact strength, Izod notched, ASTM of 117 J/m | ASTM D256 | ||
Límite elástico | 23.0 °C | 200 MPa Show Material materials with Límite elástico of 200 MPa | |||
121.0 °C | 83 MPa Show Material materials with Límite elástico of 83 MPa | ||||
Módulo de flexión | 23.0 °C | 9.38 GPa Show Material materials with Módulo de flexión of 9.38 GPa | ASTM D790 | ||
121.0 °C | 3.32 GPa Show Material materials with Módulo de flexión of 3.32 GPa | ASTM D790 | |||
Resistencia a la flexión | 23.0 °C | 276 MPa Show Material materials with Resistencia a la flexión of 276 MPa | ASTM D790 | ||
121.0 °C | 112 MPa Show Material materials with Resistencia a la flexión of 112 MPa | ASTM D790 | |||
Resistencia a la tracción | ASTM D638 | ||||
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Calor específico | 0.0 °C | 1380 J/(kg·K) Show Material materials with Calor específico of 1380 J/(kg·K) | for neat resin | ||
23.0 °C | 2 J/(kg·K) Show Material materials with Calor específico of 2 J/(kg·K) | for neat resin | |||
120.0 °C | 2300 J/(kg·K) Show Material materials with Calor específico of 2300 J/(kg·K) | for neat resin | |||
160.0 °C | 680 J/(kg·K) Show Material materials with Calor específico of 680 J/(kg·K) | for neat resin | |||
Calor latente de fusión | 188 J/g Show Material materials with Calor latente de fusión of 188 J/g | ||||
Coeficiente de dilatación térmica | 23.0 °C | 3.8E-4 1/K Show Material materials with Coeficiente de dilatación térmica of 3.8E-4 1/K | ASTM D696 | ||
Conductividad térmica | 23.0 °C | 0.23 W/(m·K) Show Material materials with Conductividad térmica of 0.23 W/(m·K) | |||
Heat deflection temperature, 0.45 MPa | 209.85 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 209.85 °C | ASTM D648 | |||
Heat deflection temperature, 1.80 MPa | 219.85 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 219.85 °C | ASTM D648 | |||
Relative temperature index, electrical | 139.85 °C Show Material materials with Relative temperature index, electrical of 139.85 °C | UL-746B; 60,000-h half-life at indicated temperature; 3.2 mm | |||
Relative temperature index, mechanical impact | 119.85 °C Show Material materials with Relative temperature index, mechanical impact of 119.85 °C | UL-746B; 60,000-h half-life at indicated temperature; 3.2 mm | |||
Relative temperature index, mechanical strength | 139.85 °C Show Material materials with Relative temperature index, mechanical strength of 139.85 °C | UL-746B; 60,000-h half-life at indicated temperature; 3.2 mm | |||
Temperatura de fusión | 219.85 °C Show Material materials with Temperatura de fusión of 219.85 °C | ASTM D789 | |||
Temperatura de transición del vidrio | 46.85 - 56.85 °C Show Material materials with Temperatura de transición del vidrio of 46.85 - 56.85 °C | ||||
Inflamabilidad | UL 94 HB (3.2mm) | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Constante dieléctrica, 1 MHz | 23.0 °C | 3.8 [-] Show Material materials with Constante dieléctrica, 1 MHz of 3.8 [-] | ASTM D150 |
Factor de disipación | 23.0 °C | 0.02 [-] Show Material materials with Factor de disipación of 0.02 [-] | ASTM D150 |
Resistividad eléctrica | 23.0 °C | 1.00E+13 Ω·m Show Material materials with Resistividad eléctrica of 1.00E+13 Ω·m | ASTM D257 |
Rigidez dieléctrica | 23.0 °C | 560 kV/mm Show Material materials with Rigidez dieléctrica of 560 kV/mm | ASTM D149, 3.2mm, short time |
Surface resistivity | 23.0 °C | 1.00E+15 Ω/sq Show Material materials with Surface resistivity of 1.00E+15 Ω/sq | ASTM D257 |
Óptico
| Property | Value | Comment |
|---|---|---|
Índice de refracción | 1.53 [-] Show Material materials with Índice de refracción of 1.53 [-] | At thickness < 0:5 mm, molded, undrawn |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Gears, fittings, and bearings. Electrical switches, bobbins, and connectors. Food packaging film. Monofilament for weed trimmers and fishing line. Blow and roto-molded containers. Wire and cable jacketing. Power tool housings, wheelchair wheels, automotive cooling fans, and other underhood parts. | |
| Fillers | 33% Glass fiber | |