Property | Temperature | Value | Thickness | Testing Standard | Condition | Comment |
---|---|---|---|---|---|---|
Absorción de agua | 7.4 % Show Supplier Material materials with Absorción de agua of 7.4 % | 2 mm | ISO 62 | immersion at 23°C | ||
Densidad | 1.32 g/cm³ Show Supplier Material materials with Densidad of 1.32 g/cm³ | ISO 1183 | dry | |||
Moisture absorption | 23 °C | 2 % Show Supplier Material materials with Moisture absorption of 2 % | 2 mm | ISO 62 | 50%RH |
Mecánica
Property | Temperature | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|---|
Elongación | 3.8 % Show Supplier Material materials with Elongación of 3.8 % | dry | ISO 527-2/1A | 5mm/min | |
6 % Show Supplier Material materials with Elongación of 6 % | 50%RH | ISO 527-2/1A | 5mm/min | ||
Módulo de flexión | 4.2 GPa Show Supplier Material materials with Módulo de flexión of 4.2 GPa | 50%RH | ISO 178 | 2mm/min | |
7.2 GPa Show Supplier Material materials with Módulo de flexión of 7.2 GPa | dry | ISO 178 | 2mm/min | ||
Módulo elástico | 5.8 GPa Show Supplier Material materials with Módulo elástico of 5.8 GPa | 50%RH | ISO 527-2/1A | 1mm/min | |
8 GPa Show Supplier Material materials with Módulo elástico of 8 GPa | dry | ISO 527-2/1A | 1mm/min | ||
Resistencia a la flexión | 155 MPa Show Supplier Material materials with Resistencia a la flexión of 155 MPa | 50%RH | ISO 178 | 2mm/min | |
250 MPa Show Supplier Material materials with Resistencia a la flexión of 250 MPa | dry | ISO 178 | 2mm/min | ||
Resistencia a la tracción | 115 MPa Show Supplier Material materials with Resistencia a la tracción of 115 MPa | 50%RH | ISO 527-2/1A | 5mm/min | |
170 MPa Show Supplier Material materials with Resistencia a la tracción of 170 MPa | dry | ISO 527-2/1A | 5mm/min | ||
Resistencia al choque, ensayo Charpy entallado | -30 °C | 9 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 9 kJ/m² | dry | ISO 179/1eA | |
23 °C | 11 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 11 kJ/m² | dry | ISO 179/1eA | ||
23 °C | 13 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 13 kJ/m² | 50%RH | ISO 179/1eA | ||
Resistencia al choque, ensayo Charpy no entallado | -30 °C | 55 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 55 kJ/m² | dry | ISO 179/1eU | |
23 °C | 65 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 65 kJ/m² | dry | ISO 179/1eU | ||
23 °C | 80 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 80 kJ/m² | 50%RH | ISO 179/1eU | ||
Resistencia al choque, ensayo Izod entallado | 23 °C | 9.7 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 9.7 kJ/m² | dry | ISO 180/1A | |
23 °C | 12 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 12 kJ/m² | 50%RH | ISO 180/1A |
Aplicaciones térmicas
Property | Value | Thickness | Testing Standard | Comment | |||
---|---|---|---|---|---|---|---|
Glow Wire Flammability Index | 650 °C Show Supplier Material materials with Glow Wire Flammability Index of 650 °C | 1 mm | IEC 60695-2-12 | ||||
675 °C Show Supplier Material materials with Glow Wire Flammability Index of 675 °C | 2 mm | IEC 60695-2-12 | |||||
Glow Wire Ignition Temperature | 675 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 675 °C | 1 mm | IEC 60695-2-13 | ||||
700 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 700 °C | 2 mm | IEC 60695-2-13 | |||||
Temperatura de flexión bajo carga | 230 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 230 °C | ISO 75/2Af | 1.80 MPa | ||||
250 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 250 °C | ISO 75/2Bf | 0.45 MPa | |||||
Temperatura de fusión | 260 °C Show Supplier Material materials with Temperatura de fusión of 260 °C | ISO 11357-1/-3 | 10°C/min | ||||
Temperatura de reblandecimiento Vicat | 250 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 250 °C | ISO 306 | 1.00E+12mm | ||||
Time-temperature limit | 140 °C Show Supplier Material materials with Time-temperature limit of 140 °C | ISO 2578 | 20000h | at 50% loss of Tensile Strength | ||||
170 °C Show Supplier Material materials with Time-temperature limit of 170 °C | ISO 2578 | 5000h | at 50% loss of Tensile Strength | |||||
Inflamabilidad | Thickness tested (mm): 2.45, Class: HB, Standard: UL 94 | Automotive Interior Flammability(mm/min): 0 ,method: ISO 3795 and thickness tested (mm): 3 |
Eléctrico
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Surface resistivity | 1e+10 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+10 Ω/sq | 50%RH | IEC 60093 | 500V |
1e+12 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq | dry | IEC 60093 | 500V | |
Volume resistivity | 1e+11 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+11 Ω·cm | 50%RH | IEC 60093 | 500V |
1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | dry | IEC 60093 | 500V | |
Índice de seguimiento comparativo | 600 V Show Supplier Material materials with Índice de seguimiento comparativo of 600 V | dry | IEC 60112 | Sol.A |
Rheological Properties
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Contracción | 0.4 % Show Supplier Material materials with Contracción of 0.4 % | 300/90/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa] |
1 % Show Supplier Material materials with Contracción of 1 % | 300/90/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa], Transverse | |
Viscosity number | 130 cm³/gr Show Supplier Material materials with Viscosity number of 130 cm³/gr | ISO 307 | Sulfuric acid |
Technological properties
Property | ||
---|---|---|
Additives | Release agent | |
Certifications | RoHS 2011/65/UE | |
Color | Natural brown | |
Features | Heat Stabilized | |
Fillers | 25% Glass Fiber | |
Processing methods | Injection Molding |