General
Property | Temperature | Value | Thickness | Testing Standard | Condition | Comment |
---|---|---|---|---|---|---|
Absorción de agua | 6.4 % Show Supplier Material materials with Absorción de agua of 6.4 % | 2 mm | ISO 62 | immersion at 23°C | ||
Densidad | 1.4 g/cm³ Show Supplier Material materials with Densidad of 1.4 g/cm³ | ISO 1183 | dry | |||
Moisture absorption | 23 °C | 1.8 % Show Supplier Material materials with Moisture absorption of 1.8 % | 2 mm | ISO 62 | 50%RH |
Mecánica
Property | Temperature | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|---|
Elongación | 3.5 % Show Supplier Material materials with Elongación of 3.5 % | dry | ISO 527-2/1A | 5mm/min | |
8 % Show Supplier Material materials with Elongación of 8 % | 50%RH | ISO 527-2/1A | 5mm/min | ||
Módulo de flexión | 6.4 GPa Show Supplier Material materials with Módulo de flexión of 6.4 GPa | 50%RH | ISO 178 | 2mm/min | |
9.8 GPa Show Supplier Material materials with Módulo de flexión of 9.8 GPa | dry | ISO 178 | 2mm/min | ||
Módulo elástico | 7.3 GPa Show Supplier Material materials with Módulo elástico of 7.3 GPa | 50%RH | ISO 527-2/1A | 1mm/min | |
11.1 GPa Show Supplier Material materials with Módulo elástico of 11.1 GPa | dry | ISO 527-2/1A | 1mm/min | ||
Resistencia a la flexión | 100 MPa Show Supplier Material materials with Resistencia a la flexión of 100 MPa | 50%RH | ISO 178 | 2mm/min | |
280 MPa Show Supplier Material materials with Resistencia a la flexión of 280 MPa | dry | ISO 178 | 2mm/min | ||
Resistencia a la tracción | 115 MPa Show Supplier Material materials with Resistencia a la tracción of 115 MPa | 50%RH | ISO 527-2/1A | 5mm/min | |
180 MPa Show Supplier Material materials with Resistencia a la tracción of 180 MPa | dry | ISO 527-2/1A | 5mm/min | ||
Resistencia al choque, ensayo Charpy entallado | -30 °C | 10 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 10 kJ/m² | dry | ISO 179/1eA | |
-30 °C | 16 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 16 kJ/m² | 50%RH | ISO 179/1eA | ||
23 °C | 14 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 14 kJ/m² | dry | ISO 179/1eA | ||
23 °C | 21 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 21 kJ/m² | 50%RH | ISO 179/1eA | ||
Resistencia al choque, ensayo Charpy no entallado | 70 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 70 kJ/m² | dry | ISO 179/1eU | -30°C | |
87 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 87 kJ/m² | dry | ISO 179/1eU | 23°C | ||
90 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 90 kJ/m² | 50%RH | ISO 179/1eU | -30°C | ||
100 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 100 kJ/m² | 50%RH | ISO 179/1eU | 23°C |
Aplicaciones térmicas
Property | Value | Testing Standard | Comment | ||
---|---|---|---|---|---|
Temperatura de flexión bajo carga | 200 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 200 °C | ISO 75/2Af | 1.80 MPa | ||
Temperatura de fusión | 220 °C Show Supplier Material materials with Temperatura de fusión of 220 °C | ISO 11357-1/-3 | 10°C/min | ||
Inflamabilidad | Automotive Interior Flammability(mm/min): 0 ,method: ISO 3795 and thickness tested (mm): 3 |
Eléctrico
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Surface resistivity | 1e+12 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq | dry | IEC 60093 | 500V |
Volume resistivity | 1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | dry | IEC 60093 | 500V |
Technological properties
Property | ||
---|---|---|
Additives | Release agent | |
Certifications | RoHS 2011/65/UE | |
Color | Black | |
Features | DPPD Free | |
Fillers | 35% Glass Fiber | |
Processing methods | Injection Molding |