Graphite AGSX

Alternative and trade names
AGSX
Want to keep this datasheet? Save it now in your required format

Description

Densified prior to graphitization, GRAFSTARTM AGSX material is good for applications requiring high densities and good mechanical properties.

This material data has been provided by Advanced Graphite Materials.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueTemperature

Density

1.72 g/cm³

Show Supplier Material materials with Density of 1.72 g/cm³ at 23.0 °C

23.0 °C

Particle size range

0.76 µm

Show Supplier Material materials with Particle size range of 0.76 µm

Porosity

16 %

Show Supplier Material materials with Porosity of 16 %

Mechanical

PropertyValueTemperature

Compressive strength

45 MPa

Show Supplier Material materials with Compressive strength of 45 MPa at 23.0 °C

23.0 °C

Elastic modulus

13 GPa

Show Supplier Material materials with Elastic modulus of 13 GPa at 23.0 °C

23.0 °C

Elastic modulus, transverse

7 GPa

Show Supplier Material materials with Elastic modulus, transverse of 7 GPa at 23.0 °C

23.0 °C

Flexural strength

23 MPa

Show Supplier Material materials with Flexural strength of 23 MPa at 23.0 °C

23.0 °C

Flexural strength, transverse

15 MPa

Show Supplier Material materials with Flexural strength, transverse of 15 MPa at 23.0 °C

23.0 °C

Tensile strength

19 MPa

Show Supplier Material materials with Tensile strength of 19 MPa at 23.0 °C

23.0 °C

Tensile strength, transverse

11 MPa

Show Supplier Material materials with Tensile strength, transverse of 11 MPa at 23.0 °C

23.0 °C

Thermal

PropertyValueTemperatureComment

Ash content

0.15 %

Show Supplier Material materials with Ash content of 0.15 % at 23.0 °C

23.0 °C

Coefficient of thermal expansion

1.2E-6 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 1.2E-6 1/K at 23.0 °C

23.0 °C

average for 20-100°C

Coefficient of thermal expansion, transverse

3.1E-6 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 3.1E-6 1/K at 23.0 °C

23.0 °C

average for 20-100°C

Thermal conductivity, in-plane

170 W/(m·K)

Show Supplier Material materials with Thermal conductivity, in-plane of 170 W/(m·K) at 23.0 °C

23.0 °C

Thermal conductivity, through-plane

120 W/(m·K)

Show Supplier Material materials with Thermal conductivity, through-plane of 120 W/(m·K) at 23.0 °C

23.0 °C

Electrical

PropertyValueTemperature

Electrical resistivity

7E-6 Ω·m

Show Supplier Material materials with Electrical resistivity of 7E-6 Ω·m at 23.0 °C

23.0 °C

Electrical resistivity, transverse

1E-5 Ω·m

Show Supplier Material materials with Electrical resistivity, transverse of 1E-5 Ω·m at 23.0 °C

23.0 °C

Technological properties

Property
Application areas

Powder metallurgy, Furnace parts

Processing history

Extruded