General
Property | Temperature | Value |
---|---|---|
Density | 23.0 °C | 8.9 g/cm³ Show Material materials with Density of 8.9 g/cm³ |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 110 - 130 GPa Show Material materials with Elastic modulus of 110 - 130 GPa | Typical for Wrought Copper High Copper Alloy |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.6E-5 - 1.8E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.6E-5 - 1.8E-5 1/K | Typical for Wrought Copper High Copper Alloy |
Melting point | 1070 - 1080 °C Show Material materials with Melting point of 1070 - 1080 °C | ||
Specific heat capacity | 23.0 °C | 360 - 420 J/(kg·K) Show Material materials with Specific heat capacity of 360 - 420 J/(kg·K) | Typical for Wrought Copper High Copper Alloy |
Thermal conductivity | 23.0 °C | 220 - 315 W/(m·K) Show Material materials with Thermal conductivity of 220 - 315 W/(m·K) |
Electrical
Property | Temperature | Value |
---|---|---|
Electrical conductivity | 23.0 °C | 3.00E+7 - 4.50E+7 S/m Show Material materials with Electrical conductivity of 3.00E+7 - 4.50E+7 S/m |
Chemical properties
Property | Value |
---|---|
Aluminium | 0.01 % Show Material materials with Aluminium of 0.01 % |
Arsenic | 0.05 % Show Material materials with Arsenic of 0.05 % |
Copper | 99.5 % Show Material materials with Copper of 99.5 % |
Iron | 0.05 % Show Material materials with Iron of 0.05 % |
Lead | 0.01 % Show Material materials with Lead of 0.01 % |
Manganese | 0.2 % Show Material materials with Manganese of 0.2 % |
Nickel | 0.3 % Show Material materials with Nickel of 0.3 % |
Other | Cu+Ag > 99.5, total 0.1, for gas welding as G-CuAg with P > 0.02%, for inert gas welding P < 0.02% |
Phosphorus | 0.01 - 0.05 % Show Material materials with Phosphorus of 0.01 - 0.05 % |
Silicon | 0.1 % Show Material materials with Silicon of 0.1 % |
Silver | 0.8 - 1.2 % Show Material materials with Silver of 0.8 - 1.2 % |