Property | Temperature | Value |
---|---|---|
Density | 23.0 °C | 8.9 g/cm³ Show Material materials with Density of 8.9 g/cm³ |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 95 - 98 GPa Show Material materials with Elastic modulus of 95 - 98 GPa | Typical for Wrought Copper Pure / Low Alloyed Copper |
Elongation | 23.0 °C | 33 % Show Material materials with Elongation of 33 % | |
Hardness, Vickers | 23.0 °C | 55 [-] Show Material materials with Hardness, Vickers of 55 [-] | |
Poisson's ratio | 23.0 °C | 0.34 [-] Show Material materials with Poisson's ratio of 0.34 [-] | Typical for Wrought Copper Pure / Low Alloyed Copper |
Shear modulus | 23.0 °C | 48 GPa Show Material materials with Shear modulus of 48 GPa | Typical for Wrought Copper Pure / Low Alloyed Copper |
Tensile strength | 23.0 °C | 200 MPa Show Material materials with Tensile strength of 200 MPa | |
Yield strength Rp0.2 | 23.0 °C | 40 MPa Show Material materials with Yield strength Rp0.2 of 40 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 20.0 °C | 1.73E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.73E-5 1/K | |
100.0 °C | 1.73E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.73E-5 1/K | ||
Melting point | 965 - 1100 °C Show Material materials with Melting point of 965 - 1100 °C | Typical for Wrought Copper Pure / Low Alloyed Copper | |
Specific heat capacity | 23.0 °C | 377 - 420 J/(kg·K) Show Material materials with Specific heat capacity of 377 - 420 J/(kg·K) | Typical for Wrought Copper Pure / Low Alloyed Copper |
Thermal conductivity | 23.0 °C | 370 W/(m·K) Show Material materials with Thermal conductivity of 370 W/(m·K) |
Electrical
Property | Temperature | Value |
---|---|---|
Electrical conductivity | 23.0 °C | 5.20E+7 S/m Show Material materials with Electrical conductivity of 5.20E+7 S/m |
Electrical resistivity | 23.0 °C | 1.92E-8 Ω·m Show Material materials with Electrical resistivity of 1.92E-8 Ω·m |
Chemical properties
Technological properties
Property | ||
---|---|---|
Brazing | soft brazing: very good | |
Workability | general (condition): very good |